Failure analysis of U71Mn rail welded joints

被引：0
|
作者：
Ma, Chuanping [1 ]
Nie, Yuan [1 ]
Wang, Lijun [1 ]
Zhu, Yonghui [1 ]
Liu, Yan [1 ]
Chen, Hui [1 ]
机构：
[1] SW Jiaotong Univ, Sch Mat Sci & Engn, Chengdu 610031, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY | 2011年 / 337卷
关键词：
U71Mn rail; oval flaw; fatigue fracture; silicate inclusions;
D O I：
10.4028/www.scientific.net/AMR.337.665
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fracture of U71Mn rail welded butt joints on flash welding was analyzed by using visual observation, metallographic microscope, SEM and EDS from macro to micro.The results show that, the transverse fracture is rail oval flaw and the fracture mechanism of the rail is fatigue-crack propagation. The fatigue cracking is caused by silicate-non-metallic inclusions which are residues in the welded joints after flash welding.
引用
收藏
页码：665 / 669
页数：5
相关论文
共 50 条
  • [41] U71Mn钢铁轨的断裂分析
    何洁玲
    广东有色金属学报, 1994, (01) : 65 - 70
  • [42] Microstructural Evolution and Micro-Corrosion Behaviour of Flash-Welded U71Mn Joints as a Function of Post-Weld Heat Treatment
    Liao, Tingting
    Zhang, Xi
    Yang, He
    Zhou, Pan
    Chen, Fei
    MATERIALS, 2023, 16 (15)
  • [43] Numerical simulation of flow, temperature and phase fields in U71Mn rail-head quenching process
    Gongfa, Li
    Jia, Liu
    Guozhang, Jiang
    Jianyi, Kong
    Liangxi, Xie
    Wentao, Xiao
    Yikun, Zhang
    Fuwei, Cheng
    Computer Modelling and New Technologies, 2014, 18 (01): : 61 - 70
  • [44] Dynamic Response and Failure Behavior of U71Mn Using a Hat-Shaped Specimen
    Wu, Jianbing
    Lu, Xu
    Wang, Zhanjiang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (03) : 2193 - 2204
  • [45] U71Mn钢轨铺设断裂失效分析
    韩晓乾
    金属加工(热加工), 2016, (05) : 70 - 71
  • [46] Dynamic Response and Failure Behavior of U71Mn Using a Hat-Shaped Specimen
    Jianbing Wu
    Xu Lu
    Zhanjiang Wang
    Journal of Materials Engineering and Performance, 2022, 31 : 2193 - 2204
  • [47] U71Mn钢轨振动疲劳寿命研究
    钟雯
    胡家杰
    刘启跃
    振动测试与诊断., 2022, 42 (05) : 893 - 897+1032
  • [48] Comparative Studies on Shear Failure Behaviors of U71Mn Rail Steel at High Strain Rates Using Hat-Shaped Specimens
    Wu, Jianbing
    Wang, Zhanjiang
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2023, 145 (01):
  • [49] U71Mn钢轨矫直断裂原因分析
    韩晓乾
    于辉
    刘帅帅
    张正伟
    理化检验(物理分册), 2015, 51 (12) : 911 - 913+917
  • [50] Study on the effect of rare earth Ce on the modification of sulfide inclusions in U71Mn heavy rail steel
    Zheng, Jie
    Liu, Shuang
    Yang, Fan
    Liu, Lixia
    Peng, Jun
    An, Shengli
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 33 : 4548 - 4556
12345