Failure analysis of U71Mn rail welded joints

被引：0
|
作者：
Ma, Chuanping [1 ]
Nie, Yuan [1 ]
Wang, Lijun [1 ]
Zhu, Yonghui [1 ]
Liu, Yan [1 ]
Chen, Hui [1 ]
机构：
[1] SW Jiaotong Univ, Sch Mat Sci & Engn, Chengdu 610031, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY | 2011年 / 337卷
关键词：
U71Mn rail; oval flaw; fatigue fracture; silicate inclusions;
D O I：
10.4028/www.scientific.net/AMR.337.665
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fracture of U71Mn rail welded butt joints on flash welding was analyzed by using visual observation, metallographic microscope, SEM and EDS from macro to micro.The results show that, the transverse fracture is rail oval flaw and the fracture mechanism of the rail is fatigue-crack propagation. The fatigue cracking is caused by silicate-non-metallic inclusions which are residues in the welded joints after flash welding.
引用
收藏
页码：665 / 669
页数：5
相关论文
共 50 条
  • [21] Simulation Study on High-Speed Milling Performance of Rail U71Mn Material
    Pan, Chao
    Zhang, Jianqiang
    He, Yuelei
    Xia, Haitao
    Wang, Baosheng
    PROCEEDINGS OF THE 3RD INTERNATIONAL CONFERENCE ON ELECTRICAL AND INFORMATION TECHNOLOGIES FOR RAIL TRANSPORTATION (EITRT) 2017: TRANSPORTATION, 2018, 483 : 967 - 974
  • [22] Strain cyclic characteristics and ratcheting of U71Mn rail steel under uniaxial loading
    Kang, G.Z.
    Gao, Q.
    Yang, X.J.
    Sun, Y.F.
    Acta Metallurgica Sinica (English Letters), 2000, 13 (03) : 893 - 900
  • [23] Super Long Life Fatigue Properties Of Rail Steel U71Mn And U75V
    Luo Zefu
    Cui Shiming
    Wu Yanzeng
    Wang Qingyuan
    MATERIAL DESIGN, PROCESSING AND APPLICATIONS, PARTS 1-4, 2013, 690-693 : 1753 - 1756
  • [24] U71Mn重轨断裂原因分析
    张里
    刘凤歧
    徐佩芳
    郭静茹
    鞍钢技术, 1992, (11) : 23 - 27
  • [25] Experimental study of the effects of temperature and humidity on the wear and damage behavior of U71Mn rail steel
    He, Chenggang
    Zhang, Peizhen
    Zhu, Runzhi
    Ye, Rongwei
    Li, Peng
    Liu, Jihua
    WEAR, 2023, 524
  • [26] Research on Rolling Wear and Damage Properties of Gas Pressure Welding Joint of U71Mn rail
    Jiang W.
    Xiang P.
    Ding H.
    Wang W.
    Liu Q.
    Guo J.
    Mocaxue Xuebao/Tribology, 2020, 40 (05): : 579 - 585
  • [27] Effect of air cooling on fatigue crack propagation speed of U71Mn heavy rail steel
    Xian, Aiping, 1600, (28):
  • [28] Numerical investigation on the rolling contact wear and fatigue of laser dispersed quenched U71Mn rail
    Zhao, Jizhong
    Miao, Hongchen
    Kan, Qianhua
    Fu, Peilin
    Ding, Li
    Kang, Guozheng
    Wang, Ping
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 143
  • [29] 包钢U71Mn钢轨Mn含量优化研究
    董捷
    梁正伟
    王永明
    郝振宇
    李永强
    魏轶彬
    包钢科技, 2022, 48 (05) : 65 - 69
  • [30] Modeling and simulation of the negative angle cutting with a combined constitutive model for U71Mn rail steel
    Zhou, Lvming
    Meng, Zhen
    Zhu, Zefei
    Tong, Kangcheng
    Cui, Zhi
    Ni, Jing
    Chen, Ziyan
    He, Qinsong
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 27 : 7852 - 7863
12345