Synergistic Effect of Addition of Fillers on Properties of Interior Waterborne UV-Curing Wood Coatings

被引：25

作者：

Yan, Xiaoxing ^{[1
]}

Qian, Xingyu ^{[1
]}

Lu, Rong ^{[2
]}

Miyakoshi, Tetsuo ^{[2
]}

机构：

[1] Nanjing Forestry Univ, Coll Furnishings & Ind Design, Nanjing 210037, Jiangsu, Peoples R China

[2] Meiji Univ, Sch Sci & Technol, Dept Ind Chem, Kawasaki, Kanagawa 2148571, Japan

来源：

COATINGS | 2018年 / 8卷 / 01期

关键词：

modification; interior waterborne coating; UV; mechanical properties; gloss; MECHANICAL-PROPERTIES; ADHESION; DURABILITY; MORPHOLOGY; STRENGTH; SILICA; RUBBER; GLOSS;

D O I：

10.3390/coatings8010009

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A waterborne ultraviolet (UV)-curing coating was prepared on the surface of wood materials with modification of talcum powder and calcium carbonate (CaCO3). When the waterborne UV-curing coatings on the surface of wood materials (WUVCW) was radiated for 1 min by UV (lambda = 365 nm) and dried at 40 degrees C for 10 min, it showed good hardness, adhesion, and impact strength, with controlling the talcum content of 2.0% and CaCO3 content of 1.0%, respectively. When the content of talcum powder was higher than 2%, the mechanical properties and gloss of the WUVCW decreased, and when the talcum powder of WUVCW increase to more than 5%, a matte surface appeared after curing. When CaCO3 and talcum powder were present at the same time, the mechanical properties of WUVCW were better than those of only CaCO3 or talcum powder.

引用

页数：13

共 50 条

[31] Synthesis of Trivinylisooctyl POSS and Its Application in UV-Curing of Polyurethane Acrylate Coatings
Wang, Yufeng
Cao, Zhenheng
Wang, Ziheng
Ma, Aijuan
[J]. COATINGS, 2022, 12 (07)
[32] Effect of addition of nanosized UV absorbers on the physico-mechanical and thermal properties of an exterior waterborne stain for wood
Cristea, Mirela Vlad
Riedl, Bernard
Blanchet, Pierre
[J]. PROGRESS IN ORGANIC COATINGS, 2011, 72 (04) : 755 - 762
[33] UV-curing process and mechanical properties of bisphenol a epoxy resin
College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
[J]. Hangkong Xuebao, 5 (1424-1432):
[34] Syntheses and UV-curing properties of organofluoro and silicone modified acrylates
Chen, Xue
Li, Yun-Qing
Wang, Jia-Xi
[J]. Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2010, 26 (12): : 16 - 19
[35] Influence of wood extracts on the UV curing of acrylate coatings
Kumar, RN
Al-Mahdi, HO
Scherzer, T
von Sonntag, J
[J]. JOURNAL OF MACROMOLECULAR SCIENCE-PURE AND APPLIED CHEMISTRY, 2002, 39 (07): : 657 - 666
[36] UV-LED Curing Efficiency of Wood Coatings
Landry, Veronic
Blanchet, Pierre
Boivin, Gabrielle
Bouffard, Jean-Francois
Vlad, Mirela
[J]. COATINGS, 2015, 5 (04): : 1019 - 1033
[37] Influence of UV-curing conditions on polymerization kinetics and gloss of urethane acrylate coatings
Jancovicova, Viera
Mikula, Milan
Havlinova, Bohuslava
Jakubikova, Zuzana
[J]. PROGRESS IN ORGANIC COATINGS, 2013, 76 (2-3) : 432 - 438
[38] Characteristics of Colorless Fluorinated Imide-Based Oligomers for UV-Curing Coatings
Park, Minseo
Moon, Hoyeon
Jung, Hyun Wook
Paik, Hyun-jong
Noh, Seung Man
[J]. ACS APPLIED POLYMER MATERIALS, 2024, 6 (17): : 11039 - 11049
[39] Epoxy coatings containing clays and organoclays: Effect of the filler and its water content on the UV-curing process
Bongiovanni, R.
Turcato, E. A.
Di Gianni, A.
Ronchetti, S.
[J]. PROGRESS IN ORGANIC COATINGS, 2008, 62 (03) : 336 - 343
[40] Effect of Microwave-Assisted Curing on Properties of Waterborne Silicone Antifouling Coatings
Li, Meng
Zhang, Zhanping
Qi, Yuhong
[J]. POLYMERS, 2022, 14 (21)

← 1 2 3 4 5 →