Measurement of Temperature Distribution in SnAg3.5 Flip-Chip Solder Joints during Current Stressing Using Infrared Microscopy

被引：0
|
作者：
Hsiao, Hsiang-Yao [1 ]
Chen, Chih [1 ]
机构：
[1] Natl Chiao Tung Univ, Dept Mat Sci & Engn, Hsinchu 30010, Taiwan
来源：
EPTC: 2008 10TH ELECTRONICS PACKAGING TECHNOLOGY CONFERENCE, VOLS 1-3 | 2008年
关键词：
D O I：
10.1109/EPTC.2008.4763505
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Several simulation studies reported that a hot spot exists in flip-chip solder bumps under accelerated electromigration. Yet, there are no experimental data to verify it. In this paper, the temperature distribution during electromigration in flip-chip SnAg3.5 solder bumps is directly inspected using infrared microscopy. Two clear hot spots are observed in the bump. One is located at the region with peak current density, and the other one is at the bump edge under the current-feeding metallization on the chip side. Under a current stress of 1.06 x 10(4) A/cm(2), the temperature in the two hot spots are 161.7 degrees C and 167.8 degrees C, respectively, which surpass the average bump temperature of 150.5 degrees C. In addition, effect of under-bump-metallization (UBM) thickness oil the hot spots is also examined. It indicates that the hot-spot temperature in the solder bump increases for the solder joints with a thinner UBM. Electromigration test indicates that these hot spots have significant influence oil the initial failure location.
引用
收藏
页码：639 / 643
页数：5
相关论文
共 50 条
  • [41] Failure mechanism of Sn-Ag-Cu flip-chip solder joints with different Cu weight contents under comparatively low current stressing
    Lai, Yi-Shao
    Chiu, Ying-Ta
    57TH ELECTRONIC COMPONENTS & TECHNOLOGY CONFERENCE, 2007 PROCEEDINGS, 2007, : 1462 - +
  • [42] Pb phase coarsening in eutectic Pb/Sn flip chip solder joints under electric current stressing
    Ye, H
    Basaran, C
    Hopkins, DC
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2004, 41 (9-10) : 2743 - 2755
  • [43] FEM modeling of temperature distribution of a flip-chip no-flow underfill package during solder reflow process
    Zhang, ZQ
    Sitaraman, SK
    Wong, CP
    IEEE TRANSACTIONS ON ELECTRONICS PACKAGING MANUFACTURING, 2004, 27 (01): : 86 - 93
  • [44] Time evolution of temperature distribution of a flip-chip no-flow underfill package during solder reflow process
    Zhang, ZQ
    Vorakunpinij, A
    Sitaraman, SK
    Wong, CP
    53RD ELECTRONIC COMPONENTS & TECHNOLOGY CONFERENCE, 2003 PROCEEDINGS, 2003, : 443 - 448
  • [45] Temperature measurement at flip chip solder joint during electromigration test
    Kimihiro Yamanaka
    Takafumi Ooyoshi
    Takayuki Nejime
    Journal of Materials Science: Materials in Electronics, 2010, 21 : 53 - 57
  • [46] Temperature measurement at flip chip solder joint during electromigration test
    Yamanaka, Kimihiro
    Ooyoshi, Takafumi
    Nejime, Takayuki
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2010, 21 (01) : 53 - 57
  • [47] Erratum: "Thermomigration in flip-chip SnPb solder joints under alternate current stressing" [Appl. Phys. Lett. 90, 152105 (2007)]
    Hsiao, Hsiang-Yao
    Chen, Chih
    APPLIED PHYSICS LETTERS, 2007, 90 (24)
  • [48] Temperature-dependent failure mechanism of SnAg solder joints with Cu metallization after current stressing: Experimentation and analysis
    Lin, C. K.
    Tsao, Wei An
    Liang, Y. C.
    Chen, Chih
    JOURNAL OF APPLIED PHYSICS, 2013, 114 (11)
  • [49] Investigation of Void Nucleation and Propagation in the Joule Heating Effect During Electromigration in Flip-Chip Solder Joints
    Chang, Y. W.
    Chiu, S. H.
    Chen, Chih
    JOURNAL OF ELECTRONIC MATERIALS, 2010, 39 (11) : 2489 - 2494
  • [50] Effect of Al-trace degradation on Joule heating during electromigration in flip-chip solder joints
    Liang, S. W.
    Chiu, S. H.
    Chen, Chih
    APPLIED PHYSICS LETTERS, 2007, 90 (08)
12345