Passive Film Observations on Interstitially Hardened 316L Stainless Steel with Nitrogen for Improved Corrosion Resistance

被引：1
|
作者：
Tailleart, N. R. [1 ]
Martin, F. J. [2 ]
Rayne, R. J. [3 ]
Kahn, H. [4 ]
Heuer, A. H. [4 ]
Natishan, P. M. [2 ]
机构：
[1] NRL, Washington, DC 20036 USA
[2] Naval Res Lab, Div Chem, Washington, DC 20375 USA
[3] Naval Res Lab, Div Mat Sci, Washington, DC 20375 USA
[4] Case Western Reserve Univ, Dept Mat Sci & Engn, Cleveland, OH 44106 USA
来源：
CRITICAL FACTORS IN LOCALIZED CORROSION 7 | 2012年 / 41卷 / 25期
关键词：
CREVICE CORROSION; CARBON SUPERSATURATION; CARBURIZATION; ALLOY-625; XPS;
D O I：
10.1149/1.3697578
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
A low temperature (420 degrees C and below), plasma-based interstitial hardening (IH) with nitrogen process on 316L austenitic stainless steels (UNS S31603) was investigated. The IH-treatment significantly improved the hardness and wear resistance for all treatment temperatures. The pitting and crevice corrosion resistance of IH-N samples treated at 370 and 395 degrees C in 0.6 M NaCl solutions was improved compared to untreated samples. XPS analysis after crevice corrosion experiments indicated that no chloride was incorporated into the passive film and a TOF-SIMS experiment showed that the IH-N surface are less reactive to oxygen than untreated 316 stainless steel.
引用
收藏
页码：59 / 66
页数：8
相关论文
共 50 条
  • [11] Effect of Grain Refinement on the Corrosion Resistance of 316L Stainless Steel
    Ura-Binczyk, Ewa
    [J]. MATERIALS, 2021, 14 (24)
  • [12] Interplay between the composition of the passive film and the corrosion resistance of citric acid-passivated AISI 316L stainless steel
    da Costa, Americo Tomas
    de Oliveira, Mara Cristina Lopes
    Antunes, Renato Altobelli
    [J]. SURFACE AND INTERFACE ANALYSIS, 2021, 53 (03) : 374 - 384
  • [13] Study on Corrosion Resistance of 316L Stainless Steel Welded Joint
    Han Liqing
    Lin Guobiao
    Wang Zidong
    Zhang Hong
    Li Feng
    You Long
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (03) : 393 - 396
  • [14] Corrosion resistance of 316L stainless steel in fuel cell electrolyte
    Chen, T.T.
    Kang, S.M.
    Li, Y.L.
    [J]. Metalurgija, 2019, 58 (01): : 99 - 102
  • [15] Study on corrosion resistance of 316l stainless steel welded joint
    Han, Liqing
    Lin, Guobiao
    Wang, Zidong
    Zhang, Hong
    Li, Feng
    You, Long
    [J]. Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (03): : 393 - 396
  • [16] Corrosion resistance of EPD nanohydroxyapatite coated 316L stainless steel
    Assadian, M.
    Jafari, H.
    Shahri, S. M. Ghaffari
    Idris, M. H.
    Gholampour, B.
    [J]. SURFACE ENGINEERING, 2014, 30 (11) : 806 - 813
  • [17] CORROSION RESISTANCE OF 316L STAINLESS STEEL IN FUEL CELL ELECTROLYTE
    Chen, T. T.
    Kang, S. M.
    Li, Y. L.
    [J]. METALURGIJA, 2019, 58 (1-2): : 99 - 102
  • [18] On the origin of passive film breakdown and metastable pitting for stainless steel 316L
    Choudhary, S.
    Kelly, R. G.
    Birbilis, N.
    [J]. CORROSION SCIENCE, 2024, 230
  • [19] Effects of welding on the passive oxide film of electropolished 316L stainless steel
    Trigwell, S
    Selvaduray, G
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 166 (01) : 30 - 43
  • [20] Microstructure and corrosion properties of nitrogen stainless steel 316L produced by hipping
    Abdel-Karim, R
    Elmahallawi, I
    El-Menshawy, K
    [J]. POWDER METALLURGY, 2004, 47 (01) : 43 - 48
12345