Compressive Behavior of Spark Plasma Sintered CNT Reinforced Al2124 and Al6061 Nanocomposites

被引：2
|
作者：
Saheb, Nouari [1 ]
机构：
[1] King Fahd Univ Petr & Minerals, Ctr Excellence Nanotechnol, Dept Mech Engn, Dhahran 31261, Saudi Arabia
来源：
ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3 | 2013年 / 652-654卷
关键词：
Spark plasma sintering; Aluminum Nanocomposites; Compressive strength; CARBON NANOTUBES; COMPOSITES;
D O I：
10.4028/www.scientific.net/AMR.652-654.33
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present study, compressive behavior of CNT reinforced Al2124 and Al6061 nanocomposites was investigated. The powders were sonicated for 30 minutes then ball milled at 200 rpm for 1 hour under argon environment. The ball milled slurry was dried and again was milled under same conditions for 15 min to disperse the agglomerated particles. The prepared powders were spark plasma sintered at 35 MPa and 450 degrees C. Sintered specimens with final dimensions of 6 mm diameter and 12 mm length were used as standard specimens for compression tests carried out at a compression rate of 0.5 mm/min. The effect of CNT addition on the compressive modulus, percentage compression, and compressive strength was investigated.
引用
收藏
页码：33 / +
页数：3
相关论文
共 50 条
  • [31] Corrosion Behavior of Spark Plasma Sintered Alumina and Al2O3-SiC-CNT Hybrid Nanocomposite
    Al-Ashwan, Zh
    Hayat, U.
    Toor, I. H.
    Hassan, Syed Fida
    Saheb, N.
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2020, 23 (05):
  • [32] Compressive Strength and Thermal Properties of Spark Plasma Sintered Al-Al2O3 Nanocomposite
    Saheb, Nouari
    Khan, Muhammad Shahzeb
    SCIENCE OF SINTERING, 2018, 50 (01) : 1 - 14
  • [33] Effect of Processing on Mechanically Alloyed and Spark Plasma Sintered Al-Al2O3 Nanocomposites
    Saheb, Nouari
    Khan, Muhammad Shahzeb
    Hakeem, Abbas Saeed
    JOURNAL OF NANOMATERIALS, 2015, 2015
  • [34] Analysis of AlSi CNT composite coating on Al6061 and SS304L substrate by plasma spray
    Kumar, R.
    Madhu, S.
    Balasubramanian, M.
    ADVANCED MANUFACTURING RESEARCH AND INTELLIGENT APPLICATIONS, 2014, 591 : 112 - +
  • [35] Workability Studies on Al6061 Alloy and Al6061 Metal Matrix Composites Reinforced with Silicon Carbide Particles Under Cold Backward Extrusion
    Venkatesh R.
    Niranjan C.A.
    Srinivas S.
    Raghavendra T.
    Journal of The Institution of Engineers (India): Series D, 2023, 104 (1) : 373 - 389
  • [36] Dry Sliding Wear Behavior of Graphite Particulate Reinforced Al6061 Alloy Composite Materials
    Nagaral, Madeva
    Auradi, V.
    Kori, S. A.
    DYNAMICS OF MACHINES AND MECHANISMS, INDUSTRIAL RESEARCH, 2014, 592-594 : 170 - +
  • [37] The effect of SiC content on the tribocorrosion performance of spark plasma sintered Al–SiC nanocomposites
    P. V. Cobbinah
    W. R. Matizamhuka
    SN Applied Sciences, 2019, 1
  • [38] SYNTHESIS AND CHARACTERIZATION OF TiO2 REINFORCED Al6061 COMPOSITES
    Kumar, G. B. Veeresh
    Gouda, P. S. Shivakumar
    Pramod, R.
    Rao, C. S. P.
    ADVANCED COMPOSITES LETTERS, 2017, 26 (01) : 18 - 23
  • [39] Experimental Investigation of Mechanical Properties of Al6061 Reinforced with Iron ore
    Marachakkanavar, Mailareppa
    Sanjey, S. J.
    Korade, D. N.
    Jagtap, K. R.
    MATERIALS TODAY-PROCEEDINGS, 2017, 4 (08) : 8219 - 8225
  • [40] Development of short fiber-reinforced NiTi/Al6061 composite
    Xie, C. L.
    Hailat, M.
    Wu, X.
    Newaz, G.
    Taya, M.
    Raju, B.
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2007, 129 (01): : 69 - 76
12345