Compressive Behavior of Spark Plasma Sintered CNT Reinforced Al2124 and Al6061 Nanocomposites

被引：2
|
作者：
Saheb, Nouari [1 ]
机构：
[1] King Fahd Univ Petr & Minerals, Ctr Excellence Nanotechnol, Dept Mech Engn, Dhahran 31261, Saudi Arabia
来源：
ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3 | 2013年 / 652-654卷
关键词：
Spark plasma sintering; Aluminum Nanocomposites; Compressive strength; CARBON NANOTUBES; COMPOSITES;
D O I：
10.4028/www.scientific.net/AMR.652-654.33
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present study, compressive behavior of CNT reinforced Al2124 and Al6061 nanocomposites was investigated. The powders were sonicated for 30 minutes then ball milled at 200 rpm for 1 hour under argon environment. The ball milled slurry was dried and again was milled under same conditions for 15 min to disperse the agglomerated particles. The prepared powders were spark plasma sintered at 35 MPa and 450 degrees C. Sintered specimens with final dimensions of 6 mm diameter and 12 mm length were used as standard specimens for compression tests carried out at a compression rate of 0.5 mm/min. The effect of CNT addition on the compressive modulus, percentage compression, and compressive strength was investigated.
引用
收藏
页码：33 / +
页数：3
相关论文
共 50 条
  • [21] S/N Ratio Analysis of Tribological Behavior of SiCp Reinforced Al2124 Based Metal Matrix Composite
    Sahin, Y.
    Oksuz, K. Emre
    ADVANCED MATERIALS RESEARCH III, 2013, 685 : 24 - +
  • [22] Microstructure and Mechanical Characterization of Al2O3/Graphene Reinforced Al6061 Based Hybrid Nanocomposites
    Sourabh Kumar Soni
    Daksh Ganatra
    Parth Mendiratta
    CH. S. K. Akhilesh Reddy
    Benedict Thomas
    Metals and Materials International, 2022, 28 : 545 - 555
  • [23] SYNTHESIS, CHARACTERIZATION AND HARDNESS STUDIES OF NANO RICE HUSK ASH REINFORCED AL6061 NANOCOMPOSITES
    Vasamsetti, Subrahmanyam
    Dumpala, Lingaraju
    Subbarao, V. V.
    JOURNAL OF ENGINEERING SCIENCE AND TECHNOLOGY, 2018, 13 (09) : 2916 - 2929
  • [24] Fracture toughness of selectively reinforced Al2124 alloy: Precrack tip in the composite side
    Milan, MT
    Bowen, P
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (04): : 1393 - 1401
  • [25] An investigation of the tensile and compressive properties of Al6061 and its nanocomposites in as-cast state and in extruded condition
    Ezatpour, H. R.
    Sajjadi, S. A.
    Sabzevar, M. H.
    Huang, Y. Z.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 607 : 589 - 595
  • [26] Wear behavior of conventional and spark plasma sintered Al2O3-NbC nanocomposites
    Alecrim, Lais
    Ferreira, Julieta
    Dolores Salvador, Maria
    Borrell, Amparo
    Pallone, Eliria
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2018, 15 (02) : 418 - 425
  • [27] Characterization of Hot Deformation Behavior of Nanosized Al2O3 Reinforced Al6061 Composites
    Yeon, Kyu Ho
    Park, Hyun Soon
    Kim, Mok Soon
    Yu, Seung Baek
    Lee, Jeong Keun
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2019, 19 (07) : 3929 - 3934
  • [28] Precipitation behavior of cold sprayed Al6061 coatings
    Mangalarapu, Tarun Babu
    Kumar, S.
    Ramakrishna, Mantripragada
    Gandham, Phanikumar
    Suresh, Koppoju
    MATERIALIA, 2022, 24
  • [29] Electrical conductivity and thermal properties of spark plasma sintered Al2O3-SiC-CNT hybrid nanocomposites
    Saheb, Nouari
    Hayat, Umer
    CERAMICS INTERNATIONAL, 2017, 43 (07) : 5715 - 5722
  • [30] Investigation on wear behaviour of AL6061 amalgam reinforced with carbides
    Vishwas, Doddabommappa Kotrappa
    Chandrappa, Chaldiganahalli Nassappa
    INTERNATIONAL CONFERENCE ON EMERGING TRENDS IN MECHANICAL ENGINEERING (ETIME-2019), 2020, 2236
12345