Effects of water vapor on corrosion behaviors of C/SiC in oxidizing atmosphere containing Na2SO4 vapor

被引：13
|
作者：
Luan, Xin'gang [1 ]
Zhang, Jun [1 ]
Cheng, Laifei [1 ]
机构：
[1] NW Polytech Univ, Sci & Technol Thermlstruct Composite Mat Lab, Xian 710072, Shaanxi, Peoples R China
来源：
COMPOSITES PART B-ENGINEERING | 2012年 / 43卷 / 08期
关键词：
Ceramic-matrix composites (CMCs); Corrosion; Damage mechanics; Electron microscopy; SIO2 SCALE VOLATILITY; SILICON-BASED CERAMICS; COMBUSTION CONDITIONS; SALT VAPOR; ENVIRONMENTS; OXIDATION; COMPOSITE; RECESSION; KINETICS; CARBIDE;
D O I：
10.1016/j.compositesb.2012.05.047
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion of a C/SiC composite has been investigated in the atmosphere containing oxygen, water vapor and sodium sulfate vapor at the temperatures range from 1000 to 1500 degrees C. The effect of water vapor on the corrosion mechanism of C/SiC were discussed based on the weight change, the residual strength change, the microstructure and calculated results from FactSage. The corrosion of C/SiC is attributed to (i) the permeation of gas through the SiO2 film below 1300 degrees C, (ii) the diffusion of oxidant through pores caused by bubbles broken in the SiO2 film above 1300 degrees C. The water vapor does not change the corrosion mechanism of C/SiC composite but the temperature range in which the corrosion mechanism works by accelerating the oxidation of SIC and the corrosion of SiO2. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2968 / 2972
页数：5
相关论文
共 50 条
  • [31] Impact of some inorganic anions on the corrosion of nickel in a solution containing Na2SO4 and NaClO4
    Deyab, M. A.
    Alghamdi, Majed M.
    El-Zahhar, Adel A.
    SCIENTIFIC REPORTS, 2024, 14 (01)
  • [32] Impact of some inorganic anions on the corrosion of nickel in a solution containing Na2SO4 and NaClO4
    M. A. Deyab
    Majed M. Alghamdi
    Adel A. El-Zahhar
    Scientific Reports, 14
  • [33] SIMS study of SiC single crystal oxidized in atmosphere containing isotopic water vapor
    Akashi, Takaya
    Kasajima, Miho
    Kiyono, Hajime
    Shimada, Shiro
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2008, 116 (1357) : 960 - 964
  • [34] Na2SO4 Induced Hot Corrosion of Aluminized Low Carbon Steel at 700 °C
    Badaruddin, Mohammad
    ADVANCES IN APPLIED MECHANICS AND MATERIALS, 2014, 493 : 761 - 766
  • [35] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050 °C
    Hongyu Wang
    Han Wang
    Peng Kan
    Qian Zhao
    Xiang Zhang
    Yang Ding
    Oxidation of Metals, 2018, 90 : 571 - 583
  • [36] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050°C
    Wang, Hongyu
    Wang, Han
    Kan, Peng
    Zhao, Qian
    Zhang, Xiang
    Ding, Yang
    OXIDATION OF METALS, 2018, 90 (5-6): : 571 - 583
  • [37] Hot Corrosion of SrTiO3 Perovskite in Na2SO4
    Prasad, M. Krishna
    Rao, K. Srinivasa
    Reddy, Madhusudhan
    Sreedhar, Gosipathala
    INTERNATIONAL JOURNAL OF CORROSION, 2018, 2018
  • [38] Hot Corrosion Behavior of ZrB2-SiC-Graphite Composite in NaCl and Na2SO4 Molten Salts
    Liu, X.
    Wang, G.
    Liu, L.
    Wang, Z.
    Wu, Z.
    Liu, M.
    JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2018, 9 (03): : 309 - 317
  • [39] A Comparative Study on Corrosion Behaviors of 15CrMo in Saline (Na2SO4) Gas Phase and Liquid Phase at 350°C
    Bai, Bing
    Deng, Lei
    Chen, Jun
    Zhang, Naifeng
    Zhao, Xuezhan
    Xiao, Gang
    Sun, Weichao
    Che, Defu
    JOM, 2022, 74 (09) : 3540 - 3547
  • [40] The high temperature corrosion of valve steels in water vapor and acetic acid containing atmosphere
    Grzesik, Zbigniew
    Migdalska, Monika
    Mrowec, Stanislaw
    OCHRONA PRZED KOROZJA, 2009, 52 (11): : 500 - 502
12345