Determination of Loading and Residual Stresses on Offshore Jacket Structures by X-ray Diffraction

被引:3
|
作者
Schubnell, Jan [1 ]
Carl, Eva [1 ]
Widerspan, Viktor [2 ]
Collmann, Mareike [3 ]
机构
[1] Fraunhofer Inst Mech Mat, Woehlerstr 11, D-79108 Freiburg, Germany
[2] Fraunhofer Inst Wind Energy Syst, Merkurstr 13, D-30419 Hannover, Germany
[3] Leibniz Univ Hannover, Fac Civil Engn & Geodet Sci, Test Ctr Support Struct, Merkurstr 13, D-30419 Hannover, Germany
关键词
offshore jacket structures; welding joints; residual stresses; fatigue loading; FATIGUE-STRENGTH; RELAXATION;
D O I
10.3390/jmse11071304
中图分类号
U6 [水路运输]; P75 [海洋工程];
学科分类号
0814 ; 081505 ; 0824 ; 082401 ;
摘要
As basements of offshore wind turbines (OWTs) in deep water (>50 m), jacket structures are an economic alternative to monopiles. For this reason, the structural durability of jackets has become more important. In such structures, welded tubular joints are weak points for fatigue design. The harmful effect of tensile residual stresses in welding joints is well known. For these reasons, the residual stresses and the loading stresses of offshore jacket structures were determined by X-ray diffraction (XRD) using a mobile diffractometer. This allows us to directly determine the load stress at the fatigue-critical locations, namely at the weld toe at the testing rig. High tensile residual stresses up to 250 MPa were determined in a welded (and unloaded) condition. At a loaded structure (10,000 load cycles), a lower residual stress level was determined. During loading, a local increase in the stress at the welded joint that is between 1.4 and 4 times higher than the applied nominal stress was determined. Furthermore, it is shown that additional treatment (grinding and clean blasting) influences the local stress state significantly.
引用
收藏
页数:10
相关论文
共 50 条
  • [21] Measurement of residual stresses in CFRP laminates by X-ray diffraction method
    Balasingh, C
    Singh, V
    BULLETIN OF MATERIALS SCIENCE, 1997, 20 (03) : 325 - 332
  • [22] Residual stresses determination and analysis in dissimilar rotary friction joints using X-ray diffraction method
    Ouali, N.
    Cheniti, B.
    Belkessa, B.
    Hassan, A. J.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2024, 80
  • [23] DETERMINATION OF RESIDUAL-STRESSES WITH A GRADIENT BY MEANS OF X-RAY-DIFFRACTION
    MELKER, AI
    PAVLOVA, VG
    INDUSTRIAL LABORATORY, 1976, 42 (03): : 376 - 378
  • [24] CONTRIBUTION TO DETERMINATION OF RESIDUAL AUSTENITE BY MEANS OF X-RAY DIFFRACTION
    BOZZOLA, A
    MOLTONI, E
    METALLURGIA ITALIANA, 1968, 60 (02): : 113 - &
  • [25] Residual stress determination in microsystems using X-ray diffraction
    Kämpfe, B
    Kämpfe, A
    Auerswald, E
    Kassem, ME
    MICRO MATERIALS, PROCEEDINGS, 2000, : 695 - 699
  • [26] X-ray diffraction analysis of residual stresses in textured ZnO thin films
    Dobrocka, E.
    Novak, P.
    Buc, D.
    Harmatha, L.
    Murin, J.
    APPLIED SURFACE SCIENCE, 2017, 395 : 16 - 23
  • [27] X-ray diffraction analysis of the structure and residual stresses of W/Cu multilayers
    Girault, B.
    Villain, P.
    Le Bourhis, E.
    Goudeau, P.
    Renault, P. -O.
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (07): : 4372 - 4376
  • [28] X-ray diffraction analysis of the residual stresses in aluminum alloys for automotive manufacturing
    Branger, V
    Briand, E
    Kusmeruck, C
    Morin, N
    Corot, F
    Auburtin, P
    JOURNAL DE PHYSIQUE IV, 2002, 12 (PR6): : 165 - 175
  • [29] Hydrogen Interaction with Residual Stresses in Steel Studied by Synchrotron X-Ray Diffraction
    Dabah, Eitan
    Kannengiesser, Thomas
    Eliezer, Dan
    Boellinghaus, Thomas
    MECHANICAL STRESS EVALUATION BY NEUTRONS AND SYNCHROTRON RADIATION VI, 2014, 772 : 91 - +