Oxidation behavior and intermetallic compound growth dynamics of SAC305/Cu solder joints under rapid thermal shock

被引：7
|
作者：
Wu, Ming [1 ]
Wang, Shan-lin [1 ]
Yin, Li-meng [2 ]
Chen, Yu-hua [1 ]
Hong, Min [1 ]
Sun, Wen-jun [1 ]
Yao, Zong-xiang [2 ]
Ni, Jia-ming [1 ]
Lu, Peng [3 ]
Zhang, Ti-ming [1 ]
Xie, Ji-lin [1 ]
机构：
[1] Nanchang Hangkong Univ, Jiangxi Key Lab Forming & Joining Technol Aerosp C, Nanchang 330063, Peoples R China
[2] Chongqing Univ Sci & Technol, Sch Met & Mat Engn, Chongqing 401331, Peoples R China
[3] Jiangxi MTC Optron Co Ltd, Nanchang 330006, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2023年 / 33卷 / 10期
基金：
中国国家自然科学基金;
关键词：
induction heating; oxide film; SAC305; intermetallic compound; shear strength; LEAD-FREE SOLDER; MICROSTRUCTURAL EVOLUTION; INTERFACIAL REACTION; COMPOSITE SOLDER; SNAGCU SOLDER; CU; SN; AG; CU6SN5; LAYER;
D O I：
10.1016/S1003-6326(23)66317-4
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Oxidation behavior of SAC305/Cu solder joints and kinetics of intermetallic compound (IMC) growth were investigated using an electromagnetic induction heating device. The results show that the solder joint undergoes oxidation when subjected to rapid thermal shock. The oxidation behavior of the solder joint itself is the main factor, which is exacerbated by the presence of the internal Cu6Sn5 IMC. The growth of the Cu6Sn5 layer is controlled by grain boundary diffusion, while that of the Cu3Sn layer is controlled by bulk diffusion. The dissolved Cu of the substrate diffuses mainly into the interfacial IMC and the interior of the solder. Under rapid thermal shock, the shear strength of the solder joint decreases substantially, by 49.2% after 72 h. The fracture mechanism changes from ductile fracture to mixed tough-brittle fracture and finally, to brittle fracture.
引用
收藏
页码：3054 / 3066
页数：13
相关论文
共 50 条
  • [41] Study on the performance of Cu foam with different porosity on SAC305 solder joints under ultrasonic-assisted soldering
    Xin Mao
    Ruhua Zhang
    Xiong Yi
    Xiaowu Hu
    Yulong Li
    Xiongxin Jiang
    Journal of Materials Science: Materials in Electronics, 2021, 32 : 28108 - 28118
  • [42] Investigation of the Mechanical Behavior of SAC305 Solder Joints at Extreme High Temperatures Using Nanoindentation
    Alam, Mohammad S.
    Hassan, K. M. Rafidh
    Fahim, Abdullah
    Wu, Jing
    Ahmed, Sudan
    Suhling, Jeffrey C.
    Lall, Pradeep
    2020 IEEE 70TH ELECTRONIC COMPONENTS AND TECHNOLOGY CONFERENCE (ECTC 2020), 2020, : 2175 - 2184
  • [43] Effect of Gold Content on the Microstructural Evolution of SAC305 Solder Joints Under Isothermal Aging
    Powers, Mike
    Pan, Jianbiao
    Silk, Julie
    Hyland, Patrick
    JOURNAL OF ELECTRONIC MATERIALS, 2012, 41 (02) : 224 - 231
  • [44] Effect of Gold Content on the Microstructural Evolution of SAC305 Solder Joints Under Isothermal Aging
    Mike Powers
    Jianbiao Pan
    Julie Silk
    Patrick Hyland
    Journal of Electronic Materials, 2012, 41 : 224 - 231
  • [45] Microstructural and compositional evolution of SAC305/TiN composite solder under thermal stressing
    Chen, Guang
    Wu, Yao-Feng
    SOLDERING & SURFACE MOUNT TECHNOLOGY, 2022, 34 (03) : 183 - 190
  • [46] Improving mechanical and electrical properties of Cu/SAC305/Cu solder joints under electromigration by using Ni nanoparticles doped flux
    M. Nasir Bashir
    A. S. M. A. Haseeb
    Journal of Materials Science: Materials in Electronics, 2018, 29 : 3182 - 3188
  • [47] Improving mechanical and electrical properties of Cu/SAC305/Cu solder joints under electromigration by using Ni nanoparticles doped flux
    Bashir, M. Nasir
    Haseeb, A. S. M. A.
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2018, 29 (04) : 3182 - 3188
  • [48] Migration induced IMC formation in SAC305 solder joints on Cu, NiAu and NiP metal layers
    Meinshausen, L.
    Fremont, H.
    Weide-Zaage, K.
    MICROELECTRONICS RELIABILITY, 2012, 52 (9-10) : 1827 - 1832
  • [49] IMC Growth and Element Diffusion in Cu/SAC305/Cu Interconnect under Electric-thermal Coupling
    Li Xuemei
    Sun Fenglian
    Liu Yang
    Zhang Hao
    Xin Tong
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (12) : 3047 - 3051
  • [50] Dynamics of corrosion on mechanical and electrical reliability of SAC305 solder joints during salt spray test
    Akoda, K. E.
    Guedon-Gracia, A.
    Deletage, J. -y.
    Plano, B.
    Fremont, H.
    MICROELECTRONICS RELIABILITY, 2023, 148
12345