Effect of long-term aging treatment on the structure and oxidation resistance of Cr coatings under high-temperature steam

被引：9
|
作者：
Xiang, Yang [1 ]
Zhao, Sha [2 ]
Liu, Chunhai [1 ]
Yang, Hongyan [3 ]
Zhang, Wei [3 ]
Wang, Hui [3 ]
Zhang, Ruiqian [3 ]
He, Hengji [1 ]
Liu, Sujuan [1 ]
机构：
[1] Chengdu Univ Technol, Coll Mat & Chem & Chem Engn, Chengdu 610059, Peoples R China
[2] Sichuan Univ, Inst Nucl Sci & Technol, Key Lab Radiat Phys & Technol, Minist Educ, Chengdu 610064, Peoples R China
[3] Nucl Power Inst China, Sci & Technol Reactor Fuel & Mat Lab, Chengdu 610213, Peoples R China
来源：
CORROSION SCIENCE | 2023年 / 212卷
关键词：
Cr coatings; Arc ion plating; Aging treatment; Steam oxidation; HIGH-ENTROPY ALLOYS; NUCLEAR-FUEL; DESIGN; SYSTEM; STEEL;
D O I：
10.1016/j.corsci.2022.110923
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Cr coatings were deposited on Zr-4 tubes by arc ion plating to explore the effect of different aging treatment times at low temperature on the steam oxidation performance of Cr coatings. The intrinsic relationship between the coating grain evolution and oxidation behavior after different aging times was analyzed by EBSD. The mid-term aging treatment improve the oxidation resistance of the Cr coating. After long-term aging treatment, a significant amount of Cr2O3 in the grain boundaries close to the Zr-4 substrate preferentially reacts with Zr, which is the reason for the serious degradation of the performance of the Cr coating.
引用
收藏
页数：11
相关论文
共 50 条
  • [31] High-temperature oxidation resistance of Ni-P and Ni-B electroless coatings on mild steel after long-term tests
    Castano, Juan G.
    Arias, Sandra
    Galvis, Oscar
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2020, 55 (01) : 83 - 89
  • [32] Effects of N Content on Microstructure and High-temperature Steam Oxidation Resistance of Cr-N Coating
    Bai Yu
    Huang Ping
    Ge Fangfang
    Huang Feng
    CHINA SURFACE ENGINEERING, 2020, 33 (02) : 87 - 96
  • [33] Microstructure, high-temperature corrosion and steam oxidation properties of Cr/CrN multilayer coatings prepared by magnetron sputtering
    Li, Zhuo
    Liu, Chunhai
    Chen, Qingsong
    Yang, Jijun
    Liu, Jiaming
    Yang, Hongyan
    Zhang, Wei
    Zhang, Ruiqian
    He, Linxin
    Long, Jianping
    Chang, Hong
    CORROSION SCIENCE, 2021, 191
  • [34] High temperature steam oxidation resistance of magnetron sputtered cralsin coatings
    Liu H.-Y.
    Zhu H.
    Dong Y.
    Ge F.-F.
    Huang F.
    Shu J.
    Surface Technology, 2021, 50 (03): : 308 - 314
  • [35] Microstructural effects on the high-temperature steam oxidation resistance of magnetron sputtered Cr-Al-Si-N quaternary coatings on zirconium coupons
    Dong, Yue
    Zhu, Han
    Ge, Fangfang
    Zhao, Gongshu
    Huang, Feng
    SURFACE & COATINGS TECHNOLOGY, 2019, 374 : 393 - 401
  • [36] THE EFFECT OF HAFNIUM ON HIGH-TEMPERATURE OXIDATION RESISTANCE
    SMEGGIL, JG
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1983, 130 (03) : C104 - C104
  • [37] Steam oxidation of aluminide coatings under high pressure and for long exposures
    Boulesteix, Claire
    Kolarik, Vladislav
    Pedraza, Fernando
    CORROSION SCIENCE, 2018, 144 : 328 - 338
  • [38] High-temperature oxidation resistance of sputtered (Al,Cr,Nb,Ta,Ti,Si) N coatings
    Kretschmer, Andreas
    Mayrhofer, Paul Heinz
    JOURNAL OF ALLOYS AND COMPOUNDS, 2025, 1010
  • [39] Mechanical and high-temperature steam oxidation properties of Cr coatings deposited via high-power impulse magnetron sputtering
    Chen, Ding
    Dai, Wei
    Liang, Daoxuan
    Wang, Qimin
    Yan, Jun
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
  • [40] Beneficial effect of sulfur state on high-temperature steam oxidation resistance in high chromium ferritic steels
    Nakai, M
    Murata, Y
    Morinaga, M
    Sasaki, Y
    MATERIALS TRANSACTIONS, 2004, 45 (03) : 865 - 869
12345