Effect of temperature on corrosion fatigue behavior of Inconel Alloy 690TT steam generator tube

被引：7
|
作者：
Li, Z. H. [1 ]
Lu, Y. H. [1 ]
You, L. [2 ]
Zhang, X. F. [1 ]
Wang, L. [2 ]
Tian, D. H. [1 ]
Zhang, W. D. [1 ]
Shoji, T. [1 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] State Key Lab Nucl Power Safety Monitoring Technol, Shenzhen 518172, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 227卷
关键词：
Alloy 690TT tube; Corrosion fatigue; Temperature; Crack initiation; Fatigue life; CRACK-GROWTH-BEHAVIOR; LOW-CYCLE FATIGUE; DISSOLVED-OXYGEN; STAINLESS-STEEL; TIN INCLUSION; MECHANISMS;
D O I：
10.1016/j.corsci.2023.111741
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of temperature on corrosion fatigue behavior of actual Alloy 690TT steam generator (SG) tubes in water environments was studied. Results demonstrated that temperature had significant influence on the for-mation and initiation mechanism of persistent slip bands (PSBs), as well as the crack propagation mode and mechanism, in water environment. With the increase of temperature, the corrosion fatigue life of SG tube decreased, more fatigue cracks initiated along the PSBs, and the synergistic effect of slip dissolution and local plasticity accelerated fatigue crack propagation. Then, the evaluation model of temperature on corrosion fatigue life was established.
引用
收藏
页数：12
相关论文
共 50 条
  • [1] Fatigue crack initiation and propagation behavior of Inconel Alloy 690TT steam generator tube
    Li, Z. H.
    Wang, X. Y.
    Hong, C.
    Lu, Y. H.
    Shoji, T.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 811
  • [2] Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Han, Y. M.
    Shoji, T.
    CORROSION SCIENCE, 2023, 212
  • [3] Cyclic deformation behavior and cracking mechanism of Inconel Alloy 690TT steam generator tube at elevated temperature
    Li, Z. H.
    Hong, C.
    Zhao, Y. G.
    Hu, Y.
    Lu, Y. H.
    Shoji, T.
    MATERIALS CHARACTERIZATION, 2022, 190
  • [4] High cycle fatigue behavior and numerical evaluation of Alloy 690TT steam generator tube
    Li, Zhenhua
    Wang, Xinyu
    Wang, Junping
    Lu, Yonghao
    Shoji, Tetsuo
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 137 (137)
  • [5] Effect of surface scratch depth on microstructure change and stress corrosion cracking behavior of alloy 690TT steam generator tube
    Wu, Bin
    Ming, Hongliang
    Zhang, Zhiming
    Meng, Fanjiang
    Li, Yifeng
    Wang, Jianqiu
    Han, En-Hou
    CORROSION SCIENCE, 2021, 192
  • [6] Effect of scratch depth on high cycle fatigue behavior of Alloy 690TT stream generator tube
    Li, Z. H.
    Wang, X. Y.
    Hong, C.
    Lu, Y. H.
    Shoji, T.
    JOURNAL OF NUCLEAR MATERIALS, 2022, 558
  • [7] Effects of foreign object damage on high-cycle fatigue behavior of Inconel Alloy 690TT steam generator tubes
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Zhang, W. D.
    Shoji, T.
    ENGINEERING FRACTURE MECHANICS, 2023, 292
  • [8] Stress corrosion behavior of scratched Alloy 690TT steam generator tube in chlorine-containing high-temperature pressurized water
    Wu, Bin
    Meng, Fanjiang
    Zhang, Zhiming
    Li, Rongbo
    Ming, Hongliang
    Wang, Jianqiu
    Han, En-Hou
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (10): : 1563 - 1574
  • [9] Evaluation of Tensile Properties of Alloy 690TT Steam Generator Tube at Room Temperature and 343 degrees C
    Eom, Ki Hyeon
    Kim, Jin Weon
    TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A, 2014, 38 (06) : 655 - 662
  • [10] Microstructure and stress corrosion cracking behavior of Alloy 690TT steam generator tubes with internal bulge defect
    Wu, Bin
    Ming, Hongliang
    Zhang, Zhiming
    Meng, Fanjiang
    He, Guangqing
    Wang, Jianqiu
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2022, 563
12345