Effect of Ce content on the hydrogen induced cracking of X80 pipeline steel

被引：13
|
作者：
Cheng, Wensen [1 ]
Song, Bo [1 ]
Mao, Jinghong [2 ]
机构：
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, Beijing 100083, Peoples R China
[2] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing 100083, Peoples R China
来源：
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY | 2023年 / 48卷 / 40期
基金：
中国国家自然科学基金;
关键词：
Ce content; Inclusion; Microstructure; Hydrogen induced cracking; Pipeline steel; RARE-EARTH-ELEMENTS; ACICULAR FERRITE; MECHANICAL-PROPERTIES; TRAPPING EFFICIENCY; MICROSTRUCTURE; INCLUSIONS; BEHAVIOR; CONSTITUENT; SENSITIVITY; MORPHOLOGY;
D O I：
10.1016/j.ijhydene.2022.12.331
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this study, the effect of Ce content on hydrogen induced cracking (HIC) of X80 pipeline steel has been investigated. The results show that as the Ce content increased from 0 wt% to 0.0042 wt%, 0.016 wt% and 0.024 wt%, the HIC susceptibility of tested steels decreased first and then increased. The steel containing 0.016 wt% Ce possessed the lowest HIC susceptibility because Ce modified inclusions, promoted the formation of acicular ferrite, and decreased the number of hydrogen traps and intergranular cracks. (c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：15303 / 15316
页数：14
相关论文
共 50 条
  • [41] SEM in situ investigation on fatigue cracking behavior of X80 pipeline steel with inclusions
    Tong, Ke
    Zeng, Yanping
    Han, Xinli
    Feng, Yaorong
    He, Xiaodong
    MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 : 1096 - +
  • [42] STRESS CORROSION CRACKING OF X80 PIPELINE STEEL AT COATING DEFECT IN ACIDIC SOIL
    Yan Maocheng
    Yang Shuang
    Xu Jin
    Sun Cheng
    Wu Tangqing
    Yu Changkun
    Ke Wei
    ACTA METALLURGICA SINICA, 2016, 52 (09) : 1133 - 1141
  • [43] Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution
    Liang, Ping
    Li, Xiaogang
    Du, Cuiwei
    Chen, Xu
    MATERIALS & DESIGN, 2009, 30 (05) : 1712 - 1717
  • [44] Effects of finish rolling deformation on hydrogen-induced cracking and hydrogen-induced ductility loss of high-vanadium TMCP X80 pipeline steel
    Li, Longfei
    Song, Bo
    Cui, Xiaokang
    Liu, Zhen
    Wang, Lei
    Cheng, Wensen
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2020, 45 (55) : 30828 - 30844
  • [45] MICROSTRUCTURE AND TOUGHNESS OF HAZ IN X80 PIPELINE STEEL WITH HIGH Nb CONTENT
    Miao Chengliang
    Shang Chengjia
    Wang Xuemin
    Hang Longfei
    Subramanian, Mani
    ACTA METALLURGICA SINICA, 2010, 46 (05) : 541 - 546
  • [46] Hydrogen Permeation and Electrochemical Corrosion Behavior of the X80 Pipeline Steel Weld
    H. B. Xue
    Y. F. Cheng
    Journal of Materials Engineering and Performance, 2013, 22 : 170 - 175
  • [47] Influence of hydrogen environment on fatigue fracture morphology of X80 pipeline steel
    Zhuo, Jingxuan
    Zhang, Chao
    Zhang, Shuai
    Chen, Liqiang
    Yang, Hongwei
    Liu, Fang
    Du, Yifan
    Lv, Liang
    Zheng, Shuqi
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 22 : 1039 - 1047
  • [48] Effect of applied potentials on stress corrosion cracking susceptibility of X80 pipeline steel in simulated soil solution
    Cheng, Yuan
    Yu, Hongying
    Zhang, Lixin
    Wang, Ying
    Meng, Xu
    Sun, Dongbai
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 920 - +
  • [49] Numerical simulation of hydrogen distribution in welded joint of X80 pipeline steel
    Yan, Chunyan
    Zhang, Genyuan
    Liu, Cuiying
    Hanjie Xuebao/Transactions of the China Welding Institution, 2015, 36 (09): : 103 - 107
  • [50] Hydrogen Permeation and Electrochemical Corrosion Behavior of the X80 Pipeline Steel Weld
    Xue, H. B.
    Cheng, Y. F.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (01) : 170 - 175
12345