Effect of Ce content on the hydrogen induced cracking of X80 pipeline steel

被引：13

作者：

Cheng, Wensen ^{[1
]}

Song, Bo ^{[1
]}

Mao, Jinghong ^{[2
]}

机构：

[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, Beijing 100083, Peoples R China

[2] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing 100083, Peoples R China

来源：

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY | 2023年 / 48卷 / 40期

基金：

中国国家自然科学基金;

关键词：

Ce content; Inclusion; Microstructure; Hydrogen induced cracking; Pipeline steel; RARE-EARTH-ELEMENTS; ACICULAR FERRITE; MECHANICAL-PROPERTIES; TRAPPING EFFICIENCY; MICROSTRUCTURE; INCLUSIONS; BEHAVIOR; CONSTITUENT; SENSITIVITY; MORPHOLOGY;

D O I：

10.1016/j.ijhydene.2022.12.331

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

In this study, the effect of Ce content on hydrogen induced cracking (HIC) of X80 pipeline steel has been investigated. The results show that as the Ce content increased from 0 wt% to 0.0042 wt%, 0.016 wt% and 0.024 wt%, the HIC susceptibility of tested steels decreased first and then increased. The steel containing 0.016 wt% Ce possessed the lowest HIC susceptibility because Ce modified inclusions, promoted the formation of acicular ferrite, and decreased the number of hydrogen traps and intergranular cracks. (c) 2023 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

引用

页码：15303 / 15316

页数：14

共 50 条

[31] Effect of SRB on corrosion behavior of X80 pipeline steel
Wan, Hong-Xia
Li, Ting-Ting
Song, Dong-Dong
Chen, Chang-Feng
Surface Technology, 2020, 49 (09): : 281 - 290
[32] Effect of Structure Pattern on the Performance of X80 Pipeline Steel
REN Yi
Journal of Iron and Steel Research(International), 2011, 18 (S1) : 874 - 877
[33] Effect of structure pattern on the performance of X80 pipeline steel
Technical Center, Anshan Iron and Steel Co. Ltd., Anshan 114001, China
Beijing Keji Daxue Xuebao, 2007, 8 (798-802):
[34] Hydrogen-Induced Cracking in CGHAZ of Welded X80 Steel under Tension Load
Gou, Jinxin
Xing, Xiao
Cui, Gan
Li, Zili
Liu, Jianguo
Deng, Xiangyuan
METALS, 2023, 13 (07)
[35] Molecular dynamics of hydrogen-induced BCC/FCC phase transition and cracking in plastic deformation of X80 duplex pipeline steel
Qiao, Gui-ying
Huang, Shu-yu
Liu, Yan-guang
Sha, Ji-tong
Bai, Ri-xin
Che, Bai-hui
Xiao, Fu-ren
Xu, Kai
Li, Ling-xiao
ENGINEERING FAILURE ANALYSIS, 2025, 170
[36] Effect of electrochemical hydrogen-charging conditions on nanomechanical properties of X80 pipeline steel
Hu, Qing
Cheng, Y. Frank
ENGINEERING FAILURE ANALYSIS, 2024, 160
[37] Effect of Rare Earth Ce on Modifying Inclusions in Al-killed X80 Pipeline Steel
Cheng, Wensen
Song, Bo
Yang, Zhanbing
Mao, Jinghong
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2022, 75 (11) : 2837 - 2846
[38] A study on bacteria-assisted cracking of X80 pipeline steel in soil environment
Wu, Tangqing
Sun, Cheng
Xu, Jin
Yan, Maocheng
Yin, Fucheng
Ke, Wei
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2018, 53 (04) : 265 - 275
[39] Effect of Rare Earth Ce on Modifying Inclusions in Al-killed X80 Pipeline Steel
Wensen Cheng
Bo Song
Zhanbing Yang
Jinghong Mao
Transactions of the Indian Institute of Metals, 2022, 75 : 2837 - 2846
[40] QUANTIFICATION OF SPLITTING IN X80 PIPELINE STEEL
Gervasyev, Alexey
Petrov, Roumen
Pyshmintsev, Igor
Huo, Chunyong
Barbaro, Frank
PROCEEDINGS OF THE 12TH INTERNATIONAL PIPELINE CONFERENCE, 2018, VOL 3, 2018,

← 1 2 3 4 5 →