Study on Acoustic Emission Characteristics of Fatigue Damage of A7N01 Aluminum Alloy for High-Speed Trains

被引：1
|
作者：
Zhu, Ronghua [1 ]
Fang, Song [1 ]
Sun, Weibing [1 ]
Chi, Dazhao [2 ]
机构：
[1] Nanjing Vocat Inst Railway Technol, Coll Locomot & Vehicle, Nanjing 210000, Peoples R China
[2] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin, Peoples R China
来源：
MATERIALS | 2023年 / 16卷 / 12期
关键词：
aluminum alloy; acoustic emission; fatigue damage; online monitoring; AE source mechanisms; CRACK-GROWTH; PROPAGATION; STEEL;
D O I：
10.3390/ma16124362
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Online monitoring of the fatigue damage process of A7N01 aluminum alloy base metal and weld seam was conducted based on acoustic emission (AE) and digital microscopic imaging technology. The AE signals were recorded during the fatigue tests and analyzed using the AE characteristic parameter method. Fatigue fracture was observed using scanning electron microscopy (SEM) to analyze the source mechanism of AE. The AE results show that the AE count and rise time can effectively predict the initiation of fatigue microcracks in A7N01 aluminum alloy. The digital image monitoring results of a notch tip verified the prediction of fatigue microcracks using the AE characteristic parameters. In addition, the AE characteristics of the A7N01 aluminum alloy under different fatigue parameters were studied, and the relationships between the AE characteristic values of the base metal and weld seam and the crack propagation rate were calculated using the seven-point recurrence polynomial method. These provide a basis for predicting the remaining fatigue damage in the A7N01 aluminum alloy. The present work indicates that AE technology can be used to monitor the fatigue damage evolution of welded aluminum alloy structures.
引用
收藏
页数：13
相关论文
共 50 条
  • [1] Effect of residual stress on fatigue behavior of welded joint of A7N01 aluminum alloy for high-speed trcion
    Ding, Sansan
    Li, Qiang
    Gou, Guoqing
    Hanjie Xuebao/Transactions of the China Welding Institution, 2016, 37 (09): : 23 - 28
  • [2] Microstructure and fatigue performance of typical 6N01 aluminum alloy welded joints for high-speed trains
    Zhou S.
    Zha T.
    Huang Y.-Q.
    An J.-L.
    Hu L.
    Wang L.
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2021, 31 (05): : 1253 - 1260
  • [3] Improving the fatigue strength of A7N01 aluminum alloy by adjusting Si content
    Gong, B. S.
    Liu, Z. J.
    Wang, Y. L.
    Zhang, Z. J.
    Zhang, P.
    Jiang, H. C.
    Rong, L. J.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 742 : 15 - 22
  • [4] Fatigue crack propagation behavior of A7N01 aluminum alloy under combined load
    Wang, Ping
    Liu, Xuesong
    Wu, Jia
    Wang, Qiang
    Hanjie Xuebao/Transactions of the China Welding Institution, 2015, 36 (10): : 91 - 94
  • [5] Effect of humidity on porosity, microstructure, and fatigue strength of A7N01S-T5 aluminum alloy welded joints in high-speed trains
    Gou, G.
    Zhang, M.
    Chen, H.
    Chen, J.
    Li, P.
    Yang, Y. P.
    MATERIALS & DESIGN, 2015, 85 : 309 - 317
  • [6] Investigation on Microstructure and Mechanical Property of the A7N01 Aluminum Alloy Welding Joint
    Yang, Shanglei
    Luo, Bin
    Lv, Renyuan
    Meng, Lichun
    Lin, Qinglin
    FRONTIERS OF ADVANCED MATERIALS AND ENGINEERING TECHNOLOGY, PTS 1-3, 2012, 430-432 : 2091 - +
  • [7] Fatigue behavior and life prediction of A7N01 aluminium alloy welded joint
    Liu Xue-song
    Zhang Liang
    Wang Lin-sen
    Wu Shuang-hui
    Fang Hong-yuan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (12) : 2930 - 2936
  • [8] Dynamic experimental studies of A6N01S-T5 aluminum alloy material and structure for high-speed trains
    Liu, Zishang
    Yu, Yangyang
    Yang, Zhe
    Wei, Yanpeng
    Cai, Junshuang
    Li, Maohui
    Huang, Chenguang
    ACTA MECHANICA SINICA, 2019, 35 (04) : 763 - 772
  • [9] Research on corrosion behavior of A6N01S-T5 aluminum alloy welded joint for high-speed trains
    Guoqing Gou
    Nan Huang
    Hui Chen
    Hongmei Liu
    Aiqin Tian
    Zhicheng Guo
    Journal of Mechanical Science and Technology, 2012, 26 : 1471 - 1476
  • [10] Research on corrosion behavior of A6N01S-T5 aluminum alloy welded joint for high-speed trains
    Gou, Guoqing
    Huang, Nan
    Chen, Hui
    Liu, Hongmei
    Tian, Aiqin
    Guo, Zhicheng
    JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY, 2012, 26 (05) : 1471 - 1476
12345