Fatigue behavior and life prediction of A7N01 aluminium alloy welded joint

被引：16
|
作者：
Liu Xue-song [1 ]
Zhang Liang [1 ]
Wang Lin-sen [1 ,2 ]
Wu Shuang-hui [1 ]
Fang Hong-yuan [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
[2] Dongfang Boiler Grp Co Ltd, Welding Proc Sect, Zigong 643001, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2012年 / 22卷 / 12期
关键词：
aluminium alloy; A7N01 aluminum alloy; welded joint; crack initiation; fatigue; fatigue life; life prediction; CRACK GROWTH-BEHAVIOR; ZN-MG ALLOY; MECHANICAL-PROPERTIES; AGING TREATMENT;
D O I：
10.1016/S1003-6326(11)61552-5
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (N-i) to fatigue life to failure(N-f) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin's model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.
引用
收藏
页码：2930 / 2936
页数：7
相关论文
共 50 条
  • [1] Effect of residual stress on fatigue behavior of welded joint of A7N01 aluminum alloy for high-speed trcion
    Ding, Sansan
    Li, Qiang
    Gou, Guoqing
    Hanjie Xuebao/Transactions of the China Welding Institution, 2016, 37 (09): : 23 - 28
  • [2] Tensile and fatigue behaviors of hybrid laser welded A7N01 alloy with repairing for railway vehicles
    Wu, Zhengkai
    Zhou, Xiru
    Ao, Ni
    Han, Xiaohui
    Zhu, Zongtao
    Wu, Shengchuan
    ENGINEERING FAILURE ANALYSIS, 2023, 143
  • [3] Tensile and fatigue behaviors of hybrid laser welded A7N01 alloy with repairing for railway vehicles
    Wu, Zhengkai
    Zhou, Xiru
    Ao, Ni
    Han, Xiaohui
    Zhu, Zongtao
    Wu, Shengchuan
    ENGINEERING FAILURE ANALYSIS, 2023, 143
  • [4] Fatigue crack propagation behavior of A7N01 aluminum alloy under combined load
    Wang, Ping
    Liu, Xuesong
    Wu, Jia
    Wang, Qiang
    Hanjie Xuebao/Transactions of the China Welding Institution, 2015, 36 (10): : 91 - 94
  • [5] Investigation on Microstructure and Mechanical Property of the A7N01 Aluminum Alloy Welding Joint
    Yang, Shanglei
    Luo, Bin
    Lv, Renyuan
    Meng, Lichun
    Lin, Qinglin
    FRONTIERS OF ADVANCED MATERIALS AND ENGINEERING TECHNOLOGY, PTS 1-3, 2012, 430-432 : 2091 - +
  • [6] Influence of Plate Thickness on the Fatigue Properties of A7N01 Aluminum Alloys Welded Joints
    Wang, Chuangang
    Lu, Yanxiang
    Shan, Qingqun
    Gou, Guoqing
    ADVANCED MATERIAL ENGINEERING (AME 2015), 2016, : 337 - 344
  • [7] Fatigue design and prediction on cruciform joint of 7N01 aluminum alloy
    Wang P.
    Mi L.
    Yu Y.
    Dong P.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (10): : 20 - 24
  • [8] Improving the fatigue strength of A7N01 aluminum alloy by adjusting Si content
    Gong, B. S.
    Liu, Z. J.
    Wang, Y. L.
    Zhang, Z. J.
    Zhang, P.
    Jiang, H. C.
    Rong, L. J.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 742 : 15 - 22
  • [9] Effect of microstructure and stress ratio on fatigue crack propagation behavior of A7N01 aluminum alloy fiber laser-VPTIG hybrid butt welded
    Wu, Shikai
    Qiao, Junnan
    Zou, Jianglin
    OPTICS AND LASER TECHNOLOGY, 2023, 162
  • [10] Fatigue strength of welded joints of 6N01 aluminium alloy extrusions
    Matsuoka, Kazuyoshi
    Uemura, Takeshi
    Kamata, Keiji
    Chiaki, Sadayoshi
    Keikinzoku Yosetsu/Journal of Light Metal Welding and Construction, 1994, 32 (05): : 1 - 8
12345