Fatigue behavior and life prediction of A7N01 aluminium alloy welded joint

被引：16
|
作者：
Liu Xue-song [1 ]
Zhang Liang [1 ]
Wang Lin-sen [1 ,2 ]
Wu Shuang-hui [1 ]
Fang Hong-yuan [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
[2] Dongfang Boiler Grp Co Ltd, Welding Proc Sect, Zigong 643001, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2012年 / 22卷 / 12期
关键词：
aluminium alloy; A7N01 aluminum alloy; welded joint; crack initiation; fatigue; fatigue life; life prediction; CRACK GROWTH-BEHAVIOR; ZN-MG ALLOY; MECHANICAL-PROPERTIES; AGING TREATMENT;
D O I：
10.1016/S1003-6326(11)61552-5
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (N-i) to fatigue life to failure(N-f) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin's model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.
引用
收藏
页码：2930 / 2936
页数：7
相关论文
共 50 条
  • [21] Review on fatigue life prediction models of welded joint
    Guozheng Kang
    Huiliang Luo
    Acta Mechanica Sinica, 2020, 36 : 701 - 726
  • [22] Study of local-zone microstructure, strength and fracture toughness of hybrid laser-metal-inert-gas-welded A7N01 aluminum alloy joint
    Wang, Xiaomin
    Li, Bo
    Li, Mingxing
    Huang, Cui
    Chen, Hui
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 688 : 114 - 122
  • [23] Fatigue life prediction of aluminum alloy welded joint based on variable precision rough set
    Zou, Li
    Yang, Xinhua
    Sun, Yibo
    Deng, Wu
    Hanjie Xuebao/Transactions of the China Welding Institution, 2013, 34 (04): : 65 - 68
  • [24] Microstructure and mechanical property of A7N01 aluminum alloy welded by laser-MIG hybrid method with assisting ultrasonic vibration
    Zhu, Zongtao
    Zhu, Quanchao
    Li, Yuanxing
    Chen, Hui
    Hanjie Xuebao/Transactions of the China Welding Institution, 2016, 37 (06): : 80 - 84
  • [25] Fatigue behavior of GMAW welded Aluminium alloy AA7020
    Bloem, C.A.
    Salvador, M.D.
    Amigó, V.
    Vicente, A.
    Revista de Metalurgia (Madrid), 2007, 43 (02): : 111 - 116
  • [26] Fatigue behavior of GMAW welded aluminium alloy AA7020
    Bloem, C. A.
    Salvador, M. D.
    Amigo, V.
    Vicente, A.
    REVISTA DE METALURGIA, 2007, 43 (02) : 111 - 116
  • [27] FATIGUE STRENGTH CHARACTERISTICS OF ALUMINIUM ALLOY FRICTION WELDED BUTT JOINT.
    Ogawa, Kouichi
    Ooue, Yoshio
    Nakayama, Hideaki
    Morimoto, Tomio
    Hasui, Atsushi
    Keikinzoku Yosetsu/Journal of Light Metal Welding and Construction, 1987, 25 (01): : 6 - 12
  • [28] Tensile and fatigue behavior of SZ, HAZ and BM in friction stir welded joint of rolled 6N01 aluminum alloy plate
    Sillapasa, K.
    Surapunt, S.
    Miyashita, Y.
    Mutoh, Y.
    Seo, N.
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 63 : 162 - 170
  • [29] Experimentally based method for fatigue life prediction of aluminium welded joints
    Pirsic, T
    FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 1309 - 1314
  • [30] Corrosion fatigue behavior and life prediction of butt-welded joint considering loading frequency
    Lu, Yan
    Wang, Haiyang
    Wang, Peipeng
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2024, 219
12345