Study on Acoustic Emission Characteristics of Fatigue Damage of A7N01 Aluminum Alloy for High-Speed Trains

被引：1

作者：

Zhu, Ronghua ^{[1
]}

Fang, Song ^{[1
]}

Sun, Weibing ^{[1
]}

Chi, Dazhao ^{[2
]}

机构：

[1] Nanjing Vocat Inst Railway Technol, Coll Locomot & Vehicle, Nanjing 210000, Peoples R China

[2] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin, Peoples R China

来源：

MATERIALS | 2023年 / 16卷 / 12期

关键词：

aluminum alloy; acoustic emission; fatigue damage; online monitoring; AE source mechanisms; CRACK-GROWTH; PROPAGATION; STEEL;

D O I：

10.3390/ma16124362

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Online monitoring of the fatigue damage process of A7N01 aluminum alloy base metal and weld seam was conducted based on acoustic emission (AE) and digital microscopic imaging technology. The AE signals were recorded during the fatigue tests and analyzed using the AE characteristic parameter method. Fatigue fracture was observed using scanning electron microscopy (SEM) to analyze the source mechanism of AE. The AE results show that the AE count and rise time can effectively predict the initiation of fatigue microcracks in A7N01 aluminum alloy. The digital image monitoring results of a notch tip verified the prediction of fatigue microcracks using the AE characteristic parameters. In addition, the AE characteristics of the A7N01 aluminum alloy under different fatigue parameters were studied, and the relationships between the AE characteristic values of the base metal and weld seam and the crack propagation rate were calculated using the seven-point recurrence polynomial method. These provide a basis for predicting the remaining fatigue damage in the A7N01 aluminum alloy. The present work indicates that AE technology can be used to monitor the fatigue damage evolution of welded aluminum alloy structures.

引用

页数：13

共 50 条

[31] Study on Characteristics of the External Aerodynamic Noise of High-Speed Trains
Jiang S.-J.
Yang S.
Wen B.-C.
Zhan M.
Dongbei Daxue Xuebao/Journal of Northeastern University, 2020, 41 (01): : 74 - 78
[32] Fatigue design and prediction on cruciform joint of 7N01 aluminum alloy
Wang P.
Mi L.
Yu Y.
Dong P.
Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (10): : 20 - 24
[33] Investigation on Double Wire Metal Inert Gas Welding of A7N01-T4 Aluminum Alloy in High-Speed Welding
Wei, Zhicheng
Xu, Rongzheng
Li, Hui
Hou, Yanxi
Guo, Xuming
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2019, 38 (2019) : 317 - 325
[34] Research on Salt Fog Corrosion Behavior of Welded Joint of 7N01-T4 Aluminum Alloy for High-speed Train
Wang, Xiaomin
Zhao, Junjing
Gou, Guoqing
ADVANCED MATERIALS, PTS 1-4, 2011, 239-242 : 2822 - +
[35] Fatigue Property of Al-5Zn-2Mg Aluminum Alloy Welding Joints Used in High-speed Trains
Ni Weiyuan
Yang Shanglei
Jia Jin
Bai Jianying
Lin Yangshenglan
RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (11) : 2774 - 2778
[36] Effect of microstructure and stress ratio on fatigue crack propagation behavior of A7N01 aluminum alloy fiber laser-VPTIG hybrid butt welded
Wu, Shikai
Qiao, Junnan
Zou, Jianglin
OPTICS AND LASER TECHNOLOGY, 2023, 162
[37] Composition Optimization Study on 7N01 Aluminum Alloy
Gao, Wenlin
Sun, Gang
Ma, Qingmei
Lu, Changde
Wang, Xiangjie
Ni, Xianpeng
Cui, Jianzhong
HIGH PERFORMANCE STRUCTURAL MATERIALS, 2018, : 179 - 188
[38] Laser weldability and aging characteristics of welds -Laser weldability of commercially available A7N01 Alloy (1)
Katayama, Seiji
Ogawa, Kaneaki
Keikinzoku Yosetsu/Journal of Light Metal Welding and Construction, 2010, 48 (12): : 5 - 16
[39] Quench Sensitivity of AA7N01 Alloy Used for High-Speed Train Body Structure
Hu Xie
Zhu Xiao
Zhou Li
Mingpu Wang
Shuo Ma
Hongyun Jiang
JOM, 2019, 71 : 1681 - 1686
[40] Quench Sensitivity of AA7N01 Alloy Used for High-Speed Train Body Structure
Xie, Hu
Xiao, Zhu
Li, Zhou
Wang, Mingpu
Ma, Shuo
Jiang, Hongyun
JOM, 2019, 71 (05) : 1681 - 1686

← 1 2 3 4 5 →