Accelerating formation of α-Al2O3 scale on a nanograined Ni-Al alloy by self-generated NiO top layer

被引：1
|
作者：
Xin, Y. C. [1 ,2 ]
Xu, W. [1 ]
Wang, W. [1 ]
Zhang, B. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
来源：
CORROSION SCIENCE | 2023年 / 224卷
关键词：
Nanostructured Ni-Al alloy; Oxidation resistance; Alfa alumina; Nucleation; NiO; ALUMINA CATALYST SUPPORTS; OXIDATION BEHAVIOR; ALPHA-ALUMINA; PHASE-TRANSFORMATION; TRANSIENT OXIDATION; THERMAL-STABILITY; SURFACE-AREA; THIN-FILMS; STRESS; MICROSTRUCTURE;
D O I：
10.1016/j.corsci.2023.111564
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Alfa (alpha)-Al2O3 is widely used to resist oxidation at high temperature. However, presence of some transient phases can reduce the oxidation resistance. Several strategies have been proposed to solve this issue. Here, we found that nucleation of alpha-Al2O3 can be accelerated by a NiO layer on the surface of nanostructured Ni-7 wt%Al alloy. The oxidation rate constant is an order of magnitude lower than that of beta-NiAl after 1000 degrees C oxidation. The enhanced growth compressive stress in scale is supposed to facilitate the alpha nucleation. This provides a novel strategy to develop advanced engineering alloys with high temperature applications.
引用
收藏
页数：11
相关论文
共 50 条
  • [21] Interfacial Strength Evaluation Between Sulfur-Segregated Al2O3 and Ni-Al Single Crystal Alloy Using Nanoindentation
    Tabata, Chihiro
    Osada, Toshio
    Ohmura, Takahito
    Yokokawa, Tadaharu
    Kawagishi, Kyoko
    Suzuki, Shinsuke
    SUPERALLOYS 2024, ISS 2024, 2024, : 598 - 605
  • [22] Preparation and evaluation of the Ni-Al catalyst derived from LDHs synthesized on γ-Al2O3 support
    Zhao, Xiaokang
    Li, Yuqing
    Xu, Yan
    Du, Xihua
    Xu, Jingjing
    CIVIL, ARCHITECTURE AND ENVIRONMENTAL ENGINEERING, VOLS 1 AND 2, 2017, : 373 - 376
  • [23] Synthesis and thermal analysis of nanocomposites based on intermetallic compounds in the Ni-Al system and Al2O3
    Yado, S.
    Zinigrad, M.
    GLASS PHYSICS AND CHEMISTRY, 2015, 41 (02) : 194 - 205
  • [24] Dispersion of NiO supported on γ-Al2O3 and TiO2/γ-Al2O3 supports
    Wang, J
    Dong, L
    Hu, YH
    Zheng, GS
    Hu, Z
    Chen, Y
    JOURNAL OF SOLID STATE CHEMISTRY, 2001, 157 (02) : 274 - 282
  • [25] Reduction of impregnated NiO/α-Al2O3 association of Al3+ ions with NiO
    Richardson, JT
    Twigg, MV
    APPLIED CATALYSIS A-GENERAL, 1998, 167 (01) : 57 - 64
  • [26] Ni-Al类水滑石的制备及其Ni/Al2O3加氢脱硫研究
    赵媛媛
    段振伟
    祁胜杰
    孟秀红
    王将
    段林海
    宋丽娟
    王强
    分子催化, 2014, 28 (05) : 418 - 426
  • [27] Pressureless infiltration of porous Al2O3/Ni compacts with 6061 Al alloy
    Lin, YJ
    Shen, TH
    COMPOSITE MATERIALS III, 2003, 249 : 37 - 44
  • [28] Effect of technological parameters on the process performance of pure Al2O3 layer of Ni–Al2O3 FGMs by self-induced EDM
    Wang, Zhenlong (wangzl@hit.edu.cn), 1600, Springer London (90): : 9 - 12
  • [29] Effect of technological parameters on the process performance of pure Al2O3 layer of Ni–Al2O3 FGMs by self-induced EDM
    Hongzheng Liu
    Zhenlong Wang
    Yukui Wang
    Huichao Li
    The International Journal of Advanced Manufacturing Technology, 2017, 90 : 3633 - 3641
  • [30] REACTIONS OF ADSORBED HYDROGEN WITH OXYGEN ON FE/AL2O3, NI/AL2O3 AND FE-NI/AL2O3 CATALYSTS
    LESNIEWSKA, E
    RYNKOWSKI, J
    PARYJCZAK, T
    PRZEMYSL CHEMICZNY, 1995, 74 (01): : 21 - 22
12345