Key parameters for low temperature warm compaction of high density iron-based P/M materials

被引：0
|
作者：
曹顺华
林信平
李炯义
谢湛
蔡志勇
机构：
[1] Central South University
[2] Changsha 410083
[3] China
[4] State Key Laboratory of Powder Metallurgy
来源：
Journal of Central South University of Technology(English Edition) | 2005年 / 04期
关键词：
iron-based P/M materials; low temperature warm compaction; lubricating mode;
D O I：
暂无
中图分类号：
TB34 [功能材料];
学科分类号：
080501 ;
摘要：
In order to reduce powder temperature to lower than 100℃ in warm compaction by changing polymer lubricant design, powder flowability, warm compacting behavior, lubricating mode as well as ultimate tensile strength after sinter-hardening and tempering were investigated systematically. By means of low temperature warm pressing and sintered hardening technique, samples with the sintered densities of 7.407.45g/cm3 and the strengths of 950 1390MPa are achieved as the early compacting pressure is 686735MPa.
引用
收藏
页码：359 / 365
页数：7
相关论文
共 50 条
  • [41] High-temperature superconductivity in iron-based compounds Preface
    Buechner, Bernd
    Hackl, Rudi
    Johrendt, Dirk
    PHYSICA STATUS SOLIDI B-BASIC SOLID STATE PHYSICS, 2017, 254 (01):
  • [42] High temperature magnetic behaviour of iron-based nanocrystalline alloys
    Randrianantoandro, N
    Labaye, I
    Berger, L
    Crisan, O
    Grafoute, M
    Calvayrac, F
    Greneche, JM
    JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2002, 4 (02): : 193 - 198
  • [43] Developments and Perspectives of Iron-based High-Temperature Superconductors
    Wen, Hai-Hu
    ADVANCED MATERIALS, 2008, 20 (19) : 3764 - 3769
  • [44] Near full density nano iron-based materials by pulse current sintering
    Yuanyuan Li
    Yan Long
    Xiaoqiang Li
    Tungwai Leo Ngai
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 2143 - 2146
  • [45] High permeability iron P/M materials for low frequency magnetic applications.
    Lefebvre, LP
    Pelletier, S
    Gelinas, C
    ADVANCES IN POWDER METALLURGY & PARTICULATE MATERIALS - 1997, 1997, : 117 - 126
  • [46] IMPROVED CORROSION RESISTANCE AND MECHANICAL PROPERTIES IN SINTERED IRON-BASED P/M MATERIALS BY APPLYING A THERMOCHEMICAL TREATMENT
    Potecasu, Florentina
    Marin, Mihaela
    Potecasu, Octavian
    Marin, Florin Bogdan
    Neacsu, Marian
    NANO, BIO AND GREEN - TECHNOLOGIES FOR A SUSTAINABLE FUTURE CONFERENCE PROCEEDINGS, SGEM 2016, VOL I, 2016, : 159 - 166
  • [47] Magnetic properties and microstructure of high density sintered iron by warm compaction using die wall lubrication
    Shin, Tajima
    Takeshi, Hattori
    Mikio, Kondoh
    Hiroshi, Okajima
    Masaki, Sugiyama
    Tadayoshi, Kikko
    Fenmo Yejin Jishu/Powder Metallurgy Technology, 2008, 26 (06): : 464 - 469
  • [48] LOW-TEMPERATURE MAGNETORESONANCE ABSORPTION IN IRON-BASED IN AMORPHOUS MAGNETICS
    BELOSOROV, DP
    VERTIY, AA
    GOLIK, AV
    TARAPOV, SI
    FIZIKA NIZKIKH TEMPERATUR, 1993, 19 (07): : 769 - 772
  • [49] PROPERTIES OF HIGH-DENSITY POWDER FORGED IRON-BASED ALLOY
    WANG, MC
    POWDER METALLURGY, 1994, 37 (03) : 201 - 205
  • [50] A low temperature iron-based phosphate potassium-ion battery
    Yang, Hui
    Liu, Zhaolu
    Zhang, Hao
    Xu, Xinyue
    Wu, Wei
    Wang, Baofeng
    Cao, Yongjie
    Zhang, Junxi
    JOURNAL OF POWER SOURCES, 2025, 634
12345