Key parameters for low temperature warm compaction of high density iron-based P/M materials

被引：0
|
作者：
曹顺华
林信平
李炯义
谢湛
蔡志勇
机构：
[1] Central South University
[2] Changsha 410083
[3] China
[4] State Key Laboratory of Powder Metallurgy
来源：
Journal of Central South University of Technology(English Edition) | 2005年 / 04期
关键词：
iron-based P/M materials; low temperature warm compaction; lubricating mode;
D O I：
暂无
中图分类号：
TB34 [功能材料];
学科分类号：
080501 ;
摘要：
In order to reduce powder temperature to lower than 100℃ in warm compaction by changing polymer lubricant design, powder flowability, warm compacting behavior, lubricating mode as well as ultimate tensile strength after sinter-hardening and tempering were investigated systematically. By means of low temperature warm pressing and sintered hardening technique, samples with the sintered densities of 7.407.45g/cm3 and the strengths of 950 1390MPa are achieved as the early compacting pressure is 686735MPa.
引用
收藏
页码：359 / 365
页数：7
相关论文
共 50 条
  • [31] High temperature hardness of steels and iron-based alloys
    Torres, H.
    Varga, M.
    Ripoll, M. Rodriguez
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 671 : 170 - 181
  • [32] Warm compaction of Al2O3 particulate reinforced powder metallurgy iron-based composite
    Ngai, TungwaiLeo
    Chen, Wei-Ping
    Xiao, Zhi-Yu
    Shao, Ming
    Zhang, Shuang-Yi
    Transactions of Nonferrous Metals Society of China (English Edition), 2002, 12 (05): : 886 - 889
  • [33] PREDICTION OF POROSITY IN IRON-BASED POWDER METALLURGY (P/M) MATERIALS USING AN IMAGE PROCESSING SOFTWARE
    Marin, Mihaela
    Potecasu, Florentina
    Marin, Florin Bogdan
    Potecasu, Octavian
    Alexandru, Petrica
    NANO, BIO AND GREEN - TECHNOLOGIES FOR A SUSTAINABLE FUTURE CONFERENCE PROCEEDINGS, SGEM 2016, VOL I, 2016, : 259 - 264
  • [34] Iron-based P/M soft magnetic material for electric devices operating at high frequencies
    Ishimine, Tomoyuki
    Maeda, Toru
    Toyoda, Haruhisa
    Mimura, Kouji
    Nishioka, Takao
    Sugimoto, Satoshi
    PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 1333 - +
  • [35] Predicting equation for adjusting glass temperature of binder used for P/M warm compaction processing
    Guo, SJ
    Lin, T
    Li, MY
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 1998, 5 (01): : 39 - 40
  • [36] Finite Element Analysis of Densification Process in High Velocity Compaction of Iron-Based Powder
    Liu, Miao
    Cao, Yan
    Nie, Chaorui
    Wang, Zhen
    Zhang, Yinhuan
    MATERIALS, 2024, 17 (13)
  • [37] Low-temperature stability and high-temperature reactivity of iron-based core-shell nanoparticles
    1600, American Chemical Society, Columbus, United States (126):
  • [38] Low-temperature stability and high-temperature reactivity of iron-based core-shell nanoparticles
    Bunker, CE
    Karnes, JJ
    JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2004, 126 (35) : 10852 - 10853
  • [39] The Effect of an Iron-based Catalyst on Coal Liquefaction at High Temperature
    Luo, H.
    Ling, K.
    Shen, J.
    ENERGY SOURCES PART A-RECOVERY UTILIZATION AND ENVIRONMENTAL EFFECTS, 2014, 36 (09) : 949 - 957
  • [40] High-temperature superconductivity in iron-based layered compounds
    Sadovskii, M. V.
    PHYSICS-USPEKHI, 2008, 51 (12) : 1201 - 1227
12345