Key parameters for low temperature warm compaction of high density iron-based P/M materials

被引：0
|
作者：
曹顺华
林信平
李炯义
谢湛
蔡志勇
机构：
[1] Central South University
[2] Changsha 410083
[3] China
[4] State Key Laboratory of Powder Metallurgy
来源：
Journal of Central South University of Technology(English Edition) | 2005年 / 04期
关键词：
iron-based P/M materials; low temperature warm compaction; lubricating mode;
D O I：
暂无
中图分类号：
TB34 [功能材料];
学科分类号：
080501 ;
摘要：
In order to reduce powder temperature to lower than 100℃ in warm compaction by changing polymer lubricant design, powder flowability, warm compacting behavior, lubricating mode as well as ultimate tensile strength after sinter-hardening and tempering were investigated systematically. By means of low temperature warm pressing and sintered hardening technique, samples with the sintered densities of 7.407.45g/cm3 and the strengths of 950 1390MPa are achieved as the early compacting pressure is 686735MPa.
引用
收藏
页码：359 / 365
页数：7
相关论文
共 50 条
  • [1] Key parameters for low temperature warm compaction of high density iron-based P/M materials
    Cao, SH
    Lin, XP
    Li, JY
    Xie, Z
    Cai, ZY
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2005, 12 (04): : 359 - 365
  • [2] Key parameters for low temperature warm compaction of high density iron-based P/M materials
    Shun-hua Cao
    Xin-ping Lin
    Jiong-yi Li
    Zhan Xie
    Zhi-yong Cai
    Journal of Central South University of Technology, 2005, 12 : 359 - 365
  • [3] Densification mechanism of warm compaction for iron-based powder materials
    Qu, Shengguan
    Li, Yuanyuan
    Xia, Wei
    Chen, Weiping
    PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 261 - +
  • [4] On the combined effect of lubrication and compaction temperature on properties of iron-based P/M parts
    Babakhani, Abolfazl
    Haerian, Ali
    Ghambari, Mohammad
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 437 (02): : 360 - 365
  • [5] Warm flow compaction behaviors of iron-based powders
    Gao H.-Y.
    Shao M.
    Qu S.-G.
    Xiao Z.-Y.
    Huanan Ligong Daxue Xuebao/Journal of South China University of Technology (Natural Science), 2010, 38 (12): : 24 - 28
  • [6] Densification of iron-based powder during warm compaction process
    Wu, Y.-C. (ycwu@hfut.edu.cn), 1600, Editorial Office of Transactions of Materials and Heat Treatment (35):
  • [7] Study on the Influence of Warm Die Compaction Behavior on the Mechanical Properties of Iron-Based Powder Materials
    Shi, Qile
    Chen, Di
    Pan, Qingqing
    Peng, Jingguang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (11) : 5655 - 5666
  • [8] High-temperature superconductivity in iron-based materials
    Paglione, Johnpierre
    Greene, Richard L.
    NATURE PHYSICS, 2010, 6 (09) : 645 - 658
  • [9] Effect of Warm Compaction and Lubricant on Microstructure and Properties of Iron-Based Alloy
    Hu, Xiaobin
    Liu, Zili
    Liu, Xiqin
    Xie, Huanjian
    Zhang, Cheng
    Zou, Yuwen
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (04) : 3382 - 3391
  • [10] Effect of Warm Compaction and Lubricant on Microstructure and Properties of Iron-Based Alloy
    Xiaobin Hu
    Zili Liu
    Xiqin Liu
    Huanjian Xie
    Cheng Zhang
    Yuwen Zou
    Journal of Materials Engineering and Performance, 2022, 31 : 3382 - 3391
12345