Flexibility of Burned Al2O3-C Due to Bending Tests at Room Temperature

被引：0
|
作者：
C.G. Aneziris [1 ]
M. Hampel [1 ]
S. Dudezig [1 ]
机构：
[1] Freiberg University of Mining and Technology
来源：
China's Refractories | 2008年 / 17卷 / 04期
关键词：
Alumina-silicon carbide-carbon; Dry ramming mixes; BF Trough; Oxidation resistance;
D O I：
暂无
中图分类号：
TQ175.1 [基础理论];
学科分类号：
0805 ; 080502 ;
摘要：
Simple three-point bending test at ambient temperature characterized the mechanical behavior of burned Al2O3-C refractories before and after thermal shock in association with the processing parameters(graphite content and coking temperature,etc.).The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture(CMOR)was registered in all specimens and real linear elastic behavior could be identified after the first load.The total deformation could be divided into two parts,plastic and elastic areas.The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3-C refractories.
引用
收藏
页码：1 / 4
页数：4
相关论文
共 50 条
  • [41] Properties and application of Al-Si metal bonded Al2O3-C slide plate
    Shi, Kai
    Zhong, Xiangchong
    Naihuo Cailiao/Refractories, 2007, 41 (03): : 205 - 207
  • [42] 金属Al/Si结合Al2O3-C滑板的使用损毁分析
    石凯
    钟香崇
    硅酸盐通报, 2008, (04) : 827 - 831+842
  • [43] Electroacoustic investigation of aqueous suspensions of raw materials for AL2O3-C refractories
    Moritz, Kirsten
    Gerlach, Nora
    Schmidt, Gert
    Aneziris, Christos G.
    CERAMICS INTERNATIONAL, 2018, 44 (15) : 18783 - 18790
  • [44] Strengthening of Al2O3-C slide gate plate refractories with microcrystalline graphite
    Wang, Heng
    Li, Yawei
    Zhu, Tianbin
    Fu, Zhengyi
    CERAMICS INTERNATIONAL, 2017, 43 (13) : 9912 - 9918
  • [45] Effect of Metallic Zn Powder on Oxidation Resistance of Al2O3-C Refractories
    LI Youqi
    China'sRefractories, 2006, (04) : 29 - 33
  • [46] Influence of bonding carbon on low carbon Al2O3-C refractory composites
    Chen, Yongqiang
    Liu, Guoqi
    Hou, Xiaojing
    Yang, Fengling
    Fan, Bingbing
    Zhang, Rui
    Li, Hongxia
    CERAMICS INTERNATIONAL, 2017, 43 (17) : 14599 - 14607
  • [47] Effect of the amount of recycled materials on properties and microstructure of the Al2O3-C materials
    Wang Jianzhu
    Zhao Junxue
    BIOTECHNOLOGY, CHEMICAL AND MATERIALS ENGINEERING II, PTS 1 AND 2, 2013, 641-642 : 321 - 324
  • [48] Strengthening of Al2O3-C slide gate plate refractories with expanded graphite
    Behera, Shantanu K.
    Mishra, Bhagirath
    CERAMICS INTERNATIONAL, 2015, 41 (03) : 4254 - 4259
  • [49] Microstructures and mechanical properties of Al2O3-C refractories with addition of microcrystalline graphite
    Wang, Heng
    Li, Yawei
    Zhu, Tianbin
    Sang, Shaobai
    Wang, Qinghu
    CERAMICS INTERNATIONAL, 2014, 40 (07) : 11139 - 11148
  • [50] Pore Structure, Permeability, and Alkali Attack Resistance of Al2O3-C Refractories
    Xu, Yibiao
    Sang, Shaobai
    Li, Yawei
    Ren, Bo
    Zhao, Lei
    Li, Yuanbing
    Li, Shujing
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (06): : 2885 - 2893
12345