Flexibility of Burned Al2O3-C Due to Bending Tests at Room Temperature

被引：0
|
作者：
C.G. Aneziris [1 ]
M. Hampel [1 ]
S. Dudezig [1 ]
机构：
[1] Freiberg University of Mining and Technology
来源：
China's Refractories | 2008年 / 17卷 / 04期
关键词：
Alumina-silicon carbide-carbon; Dry ramming mixes; BF Trough; Oxidation resistance;
D O I：
暂无
中图分类号：
TQ175.1 [基础理论];
学科分类号：
0805 ; 080502 ;
摘要：
Simple three-point bending test at ambient temperature characterized the mechanical behavior of burned Al2O3-C refractories before and after thermal shock in association with the processing parameters(graphite content and coking temperature,etc.).The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture(CMOR)was registered in all specimens and real linear elastic behavior could be identified after the first load.The total deformation could be divided into two parts,plastic and elastic areas.The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3-C refractories.
引用
收藏
页码：1 / 4
页数：4
相关论文
共 50 条
  • [31] Al2O3-C复合载体的制备及表征
    刘芳
    王筠
    李全良
    王小光
    江西化工, 2017, (04) : 87 - 89
  • [32] Tensile properties of domestic Al2O3f/Al2O3 composite at room temperature and 1000 °C
    Zhang, Ke
    Xu, Ping
    Zhang, Chao
    Li, Chenchen
    Ying, Enqing
    Xing, Ning
    Li, Mei
    Zhang, Chengyu
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2025, 53 (01): : 195 - 201
  • [33] Brittleness reduction of Al2O3-C 2 O 3-C refractories: Microstructure evolution and role of carbon fibers
    Wu, Zihao
    Chen, Junfeng
    Miao, Zheng
    Yan, Junjie
    Liu, Cheng
    Yan, Wen
    Zhang, Yu
    Zhang, Shaowei
    Li, Nan
    CERAMICS INTERNATIONAL, 2024, 50 (18) : 32163 - 32170
  • [34] A comparison of Al, Si and Al4SiC4 added to Al2O3-C refractories
    Zhang, SW
    Yamaguchi, A
    UNIFIED INTERNATIONAL TECHNICAL CONFERENCE ON REFRACTORIES (UNITECR 97), VOL 1 - 3: 5TH BIENNIAL WORLDWIDE CONGRESS - REFRACTORIES, A WORLDWIDE TECHNOLOGY, 1997, : 861 - 869
  • [35] Nanoscale toughening of low carbon Al2O3-C refractories by means of SiCnw/Al2O3 composite reinforcement
    Chong, Xiaochuan
    Luo, Jiyuan
    Ding, Donghai
    Jin, Shengli
    Xiao, Guoqing
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2023, 106 (11) : 6891 - 6910
  • [36] Effect of metal Zn powder on oxidation resistance of Al2O3-C refractories
    Li, Youqi
    Ke, Changming
    Li, Yousheng
    Li, Nan
    Naihuo Cailiao/Refractories, 2006, 40 (03): : 200 - 203
  • [37] Novel Al2O3-C Refractories with Less Residual Carbon Due to Nanoscaled Additives for Continuous Steel Casting Applications
    Roungos, Vasileios
    Aneziris, Christos G.
    Berek, Harry
    ADVANCED ENGINEERING MATERIALS, 2012, 14 (04) : 255 - 264
  • [38] Effect of antioxidants in Al2O3-C refractories on carbon pickup of ULC steel
    Ruan, GZ
    Li, N
    Wu, XJ
    AMERICAN CERAMIC SOCIETY BULLETIN, 2005, 84 (10):
  • [39] Effects of alumina sources on the microstructure and properties of nitrided Al2O3-C refractories
    Peng, Nai
    Deng, Chengji
    Zhu, Hongxi
    Li, Jun
    Wang, Shaohua
    CERAMICS INTERNATIONAL, 2015, 41 (04) : 5513 - 5524
  • [40] Microstructure of in situ Synthesized β-Sialon and β-SiC Bonded Al2O3-C Refractory
    Peng Nai
    Deng Chengji
    Zhu Hongxi
    Yuan Wenjie
    Hu Chen
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 : 908 - 910
12345