Phase Evolution during the Sintering of Submicron Ti(C,N)-Based Cermets

被引：3
|
作者：
Chenhui Li
机构：
来源：
Rare Metals | 2001年 / 04期
基金：
中国国家自然科学基金;
关键词：
submicron; cermet; phase; sintering;
D O I：
暂无
中图分类号：
TQ174 [陶瓷工业];
学科分类号：
0805 ; 080502 ;
摘要：
The submicron powder mixtures of TiC-TiN-WC-Mo-C-Ni sintered at 1400℃ or below in vacuum were studied by X-ray diffration （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） analyses. The results showed that Mo2C fOrmed at 800℃ or below. Both WC and Mo2C disappeared at 1200 ℃, and TiN disappeared at 1250℃. In addihon, the variahons of lanice constans of the htanium carbonitride and nickel binder phase with sintering temperature were experimentally obtained, and the reason was analyzed.
引用
收藏
页码：248 / 254
页数：7
相关论文
共 50 条
  • [41] The influence of low pressure sintering temperature on microstructure and properties of Ti(C, N)-based cermets
    Li, Ping-Ping
    Ye, Jin-Wen
    Liu, Ying
    Zou, Hong-Wei
    Yang, Jia
    Gongneng Cailiao/Journal of Functional Materials, 2010, 41 (10): : 1724 - 1726
  • [42] Microstructure and performance of functionally gradient Ti(C, N)-based cermets fabricated by low-pressure carburizing treatment during liquid phase sintering
    Zhao, Yijie
    Zheng, Yong
    Zhou, Wei
    Zhang, Jiajie
    Zhang, Guotao
    Xiong, Weihao
    CERAMICS INTERNATIONAL, 2017, 43 (02) : 1956 - 1962
  • [43] Comparative study of the fabrication of ultrafine Ti(C,N)-based cermets by spark plasma sintering and conventional vacuum sintering
    LEI Yan1)
    Rare Metals, 2005, (02) : 131 - 136
  • [44] Comparative study of the fabrication of ultrafine Ti(C,N)-based cermets by spark plasma sintering and conventional vacuum sintering
    Lei, Y
    Xiong, WH
    Liang, ZG
    Feng, P
    Wang, ZW
    RARE METALS, 2005, 24 (02) : 131 - 136
  • [45] Spark plasma sintering of Ti(C,N) cermets with intermetallic binder phases
    Alvarez, M.
    Sanchez, J. M.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2007, 25 (01): : 107 - 118
  • [46] Microstructure and properties of the cermets based on Ti(C, N)
    Zhou, Shiquan
    Zhao, Wei
    Xiong, Weihao
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2009, 27 (01): : 26 - 32
  • [47] Microstructure evolution and densification behavior of cellular Ti(C, N)-based cermets prepared by multiphase flow agglomeration and subsequent vacuum sintering
    Jiang, Zhiyi
    Zheng, Yong
    Wang, Wangwang
    Li, Bo
    Yang, Min
    Zhao, Yijie
    Zhou, Wei
    CERAMICS INTERNATIONAL, 2024, 50 (13) : 24186 - 24194
  • [48] MICROSTRUCTURE AND PROPERTIES OF THE CERMETS BASED ON Ti(C,N)
    Zhou, S. Q.
    Zhao, W.
    Xiong, W. H.
    MECHANICAL PROPERTIES AND PROCESSING OF CERAMIC BINARY,TERNARY, AND COMPOSITE SYSTEMS, 2009, 29 (02): : 41 - 50
  • [49] Effect of ball-milling time on the microstructure and mechanical properties of submicron Ti(C,N)-based cermets
    Zhou, Huijun
    Huang, Chuanzhen
    Zou, Bin
    Liu, Hanlian
    Zhu, Hongtao
    Yao, Peng
    Wang, Jun
    ADVANCES IN MACHINING AND MANUFACTURING TECHNOLOGY XII, 2014, 589-590 : 584 - 589
  • [50] Tribological behavior of Ti(C, N)-based and functionally gradient Ti(C, N)-based cermets
    Shi, Zengmin
    Feng, Ping
    Liu, Wenjun
    Zheng, Yong
    Li, Jian
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 1097 - +
12345