Low temperature bonding of LD31 aluminum alloys by electric brush plating Ni and Cu coatings

被引：1
|
作者：
赵振清
王春青
杜淼
机构：
[1] Harbin Welding Institute
[2] Harbin Institute of Technology
[3] Microjoining Laboratory
[4] School of Material Science and Engineering
来源：
China Welding | 2005年 / 01期
关键词：
LD31 aluminum alloy; electric brush plating; coating; soldering;
D O I：
暂无
中图分类号：
TG174.4 [金属表面防护技术];
学科分类号：
080503 ;
摘要：
Soldering of LD31 aluminum alloys using Sn-Pb solder paste after electric brush plating Ni and Cu coatings was investigated. The technology of electric brush plating Ni and Cu was studied and plating solution was developed. The microstructure of the coatings, soldered joint and fracture face were analyzed using optic microscopy, SEM and EDX. The shear strength of soldered joint could reach as high as 26.83MPa. The results showed that reliable soldered joint could be obtained at 230℃, the adhesion of coatings and LD31 aluminum alloy substrate was high enough to bear the thermal process in the soldering.
引用
收藏
页码：24 / 28
页数：5
相关论文
共 50 条
  • [41] Application of Ni and Cu nanoparticles in transient liquid phase (TLP) bonding of Ti-6Al-4V and Mg-AZ31 alloys
    Anas M. Atieh
    Tahir I. Khan
    Journal of Materials Science, 2014, 49 : 7648 - 7658
  • [42] Application of Ni and Cu nanoparticles in transient liquid phase (TLP) bonding of Ti-6Al-4V and Mg-AZ31 alloys
    Atieh, Anas M.
    Khan, Tahir I.
    JOURNAL OF MATERIALS SCIENCE, 2014, 49 (22) : 7648 - 7658
  • [43] Characterization and reliability study of low temperature hermetic wafer level bonding using In/Sn interlayer and Cu/Ni/Au metallization
    Yu, Da-Quan
    Lee, Chengkuo
    Yan, Li Ling
    Thew, Meei Ling
    Lau, John H.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 485 (1-2) : 444 - 450
  • [44] Evolution of martensitic transformation in Cu-Al-Ni shape memory alloys during low-temperature aging
    Recarte, V
    Pérez-Sáez, RB
    Nó, ML
    San Juan, J
    JOURNAL OF MATERIALS RESEARCH, 1999, 14 (07) : 2806 - 2813
  • [45] Low-temperature superelasticity and elastocaloric effect in textured Ni-Mn-Ga-Cu shape memory alloys
    Guo, Jianping
    Wei, Zhiyang
    Shen, Yi
    Zhang, Yifei
    Li, Jinyang
    Hou, Xueling
    Liu, Jian
    SCRIPTA MATERIALIA, 2020, 185 (185) : 56 - 60
  • [46] Characterization and reliability study of low temperature hermetic wafer level bonding using In/Sn interlayer and Cu/Ni/Au metallization
    Yu, Da-Quan
    Lee, Chengkuo
    Yan, Li Ling
    Thew, Meei Ling
    Lau, John H.
    Journal of Alloys and Compounds, 2009, 485 (1-2): : 444 - 450
  • [47] Design and Development of Ti-Ni, Ni-Mn-Ga and Cu-Al-Ni-based Alloys with High and Low Temperature Shape Memory Effects
    Pushin, Vladimir
    Kuranova, Nataliya
    Marchenkova, Elena
    Pushin, Artemy
    MATERIALS, 2019, 12 (16)
  • [48] High temperature oxidation of the three-phase alloys Cu-20Ni-30Cr and Cu-20Ni-40Cr under a low oxygen pressure
    Zhang, XJ
    Al-Omary, M
    Niu, Y
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2005, 24 (03) : 175 - 182
  • [49] Room temperature huge magnetocaloric properties in low hysteresis ordered Cu-doped Ni-Mn-In-Co alloys
    La Roca, Paulo
    Lopez-Garcia, Javier
    Sanchez-Alarcos, Vicente
    Recarte, Vicente
    Rodriguez-Velamazan, Jose Alberto
    Perez-Landazabal, Jose Ignacio
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 922
  • [50] PREFERENTIAL SPUTTERING OF CU-NI ALLOYS AT LOW-TEMPERATURE USING LOWER ENERGY AUGER-ELECTRON SPECTRA
    KOSHIKAWA, T
    GOTO, K
    SAEKI, N
    SHIMIZU, R
    SUGATA, E
    SURFACE SCIENCE, 1979, 79 (02) : 461 - 469
12345