Effects of Four Kinds of Alumina Micropowder on Properties of Al2O3-C Refractories

被引：0
|
作者：
SHEN Mingke [1 ]
LUO Ming [1 ]
HU Chengyang [1 ]
YU Yan [1 ]
SONG Yanan [1 ]
NI Feijiang [1 ]
LI Jin [1 ]
机构：
[1] Zhejiang Zili High Temperature Technology Co., Ltd.
来源：
China'sRefractories | 2022年 / 31卷 / 04期
关键词：
D O I：
10.19691/j.cnki.1004-4493.2022.04.007
中图分类号：
TQ175.1 [基础理论];
学科分类号：
0805 ; 080502 ;
摘要：
In order to further improve the strength and the thermal shock resistance of Al2O3-C materials for steel ladle slide gates,the effects of four kinds of alumina micropowders(unimodal activated alumina micropowder 07RAL, unimodal activated alumina micropowder 15RA, bimodal activated alumina micropowder 22RABL, and calcined alumina micropowder 40CA) on the density, the strength and the thermal shock resistance of Al2O3-C materials were studied. The results show that the density,the strength and the thermal shock resistance of Al2O3-C materials can be improved with the introduction of activated alumina micropowders. Among them, the specimen with bimodal activated alumina micropowder shows the best comprehensive performance, especially the hot modulus of rupture. Its actual application results in steel mills show that the average service life of the Al2O3-C slide plates prolongs, and the problems of cast hole reaming, plate oxidation, roughening and cracking during the use of slide plates are obviously improved.
引用
收藏
页码：34 / 38
页数：5
相关论文
共 50 条
  • [31] Effect of Metallic Zn Powder on Oxidation Resistance of Al2O3-C Refractories
    LI Youqi
    China'sRefractories, 2006, (04) : 29 - 33
  • [32] Microstructures and mechanical properties of Al2O3-C refractories with addition of multi-walled carbon nanotubes
    Luo, Ming
    Li, Yawei
    Jin, Shengli
    Sang, Shaobai
    Zhao, Lei
    Li, Yuanbing
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 548 : 134 - 141
  • [33] Pore Structure, Permeability, and Alkali Attack Resistance of Al2O3-C Refractories
    Xu, Yibiao
    Sang, Shaobai
    Li, Yawei
    Ren, Bo
    Zhao, Lei
    Li, Yuanbing
    Li, Shujing
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (06): : 2885 - 2893
  • [34] Pore Structure, Permeability, and Alkali Attack Resistance of Al2O3-C Refractories
    Yibiao Xu
    Shaobai Sang
    Yawei Li
    Bo Ren
    Lei Zhao
    Yuanbing Li
    Shujing Li
    Metallurgical and Materials Transactions A, 2014, 45 : 2885 - 2893
  • [35] Effect of h-BN on Microstructure and Properties of Al2O3-C Refractories at Different Nitriding Temperatures
    Chen T.
    Wang X.
    Liu Z.
    Deng C.
    Yu C.
    Ding J.
    Zhu H.
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2022, 50 (12): : 3305 - 3313
  • [36] Properties of Self-Glazing Al2O3-C Refractories Influenced by the Graphite Content and Nanoscaled Additives
    Ludwig, Susann
    Roungos, Vasileios
    Aneziris, Christos G.
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2014, 11 (06) : 961 - 967
  • [37] Effect of the reactivity and porous structure of expanded graphite (EG) on microstructure and properties of Al2O3-C refractories
    20152300902692
    Li, Yawei, 1600, Elsevier Ltd (645):
  • [38] Influences of ZrO2-SiC composite powder and commercial SiC on properties of Al2O3-C refractories
    Ma, Beiyue
    Tan, Cheng
    Yu, Jingkun
    Naihuo Cailiao/Refractories, 2007, 41 (06): : 454 - 456
  • [39] Carbon pickup of interstitial free steel from Al2O3-C refractories
    Ruan, GZ
    Li, N
    IRONMAKING & STEELMAKING, 2004, 31 (04) : 342 - 344
  • [40] Effect of Nano Carbon Black and Graphite Flake on Properties of Low Carbon Al2O3-C Refractories
    LIAO Ning
    LI Yawei
    SANG Shaobai
    CHEN Songlin
    ZENG Luju
    China'sRefractories, 2016, 25 (02) : 17 - 24
12345