Effects of Four Kinds of Alumina Micropowder on Properties of Al2O3-C Refractories

被引：0

作者：

SHEN Mingke ^{[1
]}

LUO Ming ^{[1
]}

HU Chengyang ^{[1
]}

YU Yan ^{[1
]}

SONG Yanan ^{[1
]}

NI Feijiang ^{[1
]}

LI Jin ^{[1
]}

机构：

[1] Zhejiang Zili High Temperature Technology Co., Ltd.

来源：

China'sRefractories | 2022年 / 31卷 / 04期

关键词：

D O I：

10.19691/j.cnki.1004-4493.2022.04.007

中图分类号：

TQ175.1 [基础理论];

学科分类号：

0805 ; 080502 ;

摘要：

In order to further improve the strength and the thermal shock resistance of Al2O3-C materials for steel ladle slide gates,the effects of four kinds of alumina micropowders(unimodal activated alumina micropowder 07RAL, unimodal activated alumina micropowder 15RA, bimodal activated alumina micropowder 22RABL, and calcined alumina micropowder 40CA) on the density, the strength and the thermal shock resistance of Al2O3-C materials were studied. The results show that the density,the strength and the thermal shock resistance of Al2O3-C materials can be improved with the introduction of activated alumina micropowders. Among them, the specimen with bimodal activated alumina micropowder shows the best comprehensive performance, especially the hot modulus of rupture. Its actual application results in steel mills show that the average service life of the Al2O3-C slide plates prolongs, and the problems of cast hole reaming, plate oxidation, roughening and cracking during the use of slide plates are obviously improved.

引用

页码：34 / 38

页数：5

共 50 条

[21] Properties of Low-carbon Al2O3-C Refractories with Different Critical Particle Size
Niu, Chongchong
Liu, Guoqi
Wu, Xiaoxian
Yu, Jianbin
Qin, Hongbin
ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3, 2012, 217-219 : 318 - +
[22] Microstructure and mechanical properties of lightweight Al2O3-C refractories using different carbon sources
Chen, Zhe
Yan, Wen
Schaffoner, Stefan
Li, Yawei
Li, Nan
JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 862
[23] Effect of Addition of Fused Alumina Zirconia on the Properties of Unfired Al2O3-C Slide
Wei, Juncong
Ai, Li
Ji, Xiumei
Tu, Junbo
ADVANCED ENGINEERING MATERIALS III, PTS 1-3, 2013, 750-752 : 550 - 553
[24] Effect of metal Zn powder on oxidation resistance of Al2O3-C refractories
Li, Youqi
Ke, Changming
Li, Yousheng
Li, Nan
Naihuo Cailiao/Refractories, 2006, 40 (03): : 200 - 203
[25] Effect of ZrC Modified Graphite on Structure and Properties of Low-carbon Al2O3-C Refractories
HU Chen
WANG Xing
LIU Zhenglong
DING Jun
YU Chao
DENG Chengji
China'sRefractories, 2024, 33 (01) : 18 - 22
[26] Effect of antioxidants in Al2O3-C refractories on carbon pickup of ULC steel
Ruan, GZ
Li, N
Wu, XJ
AMERICAN CERAMIC SOCIETY BULLETIN, 2005, 84 (10):
[27] Electroacoustic investigation of aqueous suspensions of raw materials for AL2O3-C refractories
Moritz, Kirsten
Gerlach, Nora
Schmidt, Gert
Aneziris, Christos G.
CERAMICS INTERNATIONAL, 2018, 44 (15) : 18783 - 18790
[28] Strengthening of Al2O3-C slide gate plate refractories with microcrystalline graphite
Wang, Heng
Li, Yawei
Zhu, Tianbin
Fu, Zhengyi
CERAMICS INTERNATIONAL, 2017, 43 (13) : 9912 - 9918
[29] Influences of ZrO2-SiC Composite Powder and Commercial SiC on Properties of Al2O3-C Refractories
MA Beiyue
China'sRefractories, 2008, (03) : 18 - 21
[30] Strengthening of Al2O3-C slide gate plate refractories with expanded graphite
Behera, Shantanu K.
Mishra, Bhagirath
CERAMICS INTERNATIONAL, 2015, 41 (03) : 4254 - 4259

← 1 2 3 4 5 →