A new composite material produced by semi-continuous casting

被引：0
|
作者：
Huixue JIANG
机构：
来源：
Acta Metallurgica Sinica(English Letters) | 2010年 / 23卷 / 04期
关键词：
Composite material; 1xxx aluminum alloy; 7xxx aluminum alloy; Semi-continuous casting;
D O I：
暂无
中图分类号：
TG249.7 [连续、半连续铸造];
学科分类号：
080201 ; 080503 ;
摘要：
A new composite material consisting of 1xxx aluminum alloy and 7xxx aluminum alloy was produced by semi-continuous casting. Macrostructure, microstructure, composition distribution and hardness distribution of composite interface were analyzed. Macrostructure shows that composite interface is planar and clean with little evidence of porosity; microstructure shows that composite interface is a kind of metallurgical bonding; composition and hardness distributions have a good corresponding relationship. At the same time, the mechanical property of composite interface was measured, the tensile strength is 71 MPa, the shearing strength is 62 MPa and the bending strength is 142.5 MPa, which can also show that composite interface is a kind of metallurgical bonding. Temperature distribution of composite interface was obtained by measuring temperatures near composite interface in 1xxx aluminum alloy.
引用
收藏
页码：255 / 260
页数：6
相关论文
共 50 条
  • [21] Dynamic response of semi-continuous composite beams
    Uy, B
    Belcour, PFG
    [J]. MECHANICS OF STRUCTURES AND MATERIALS, 1999, : 613 - 618
  • [22] Serviceability of semi-continuous composite beams in buildings
    Uy, B
    Belcour, PFG
    [J]. COMPOSITE AND HYBRID STRUCTURES, VOLS 1 AND 2, 2000, : 623 - 630
  • [23] Casting and remelted microstructures of 7075 alloy cast by liquidus semi-continuous casting
    Lu, G.
    Dong, J.
    Cui, J.
    [J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2001, 11 (02): : 211 - 215
  • [24] HORIZONTAL SEMI-CONTINUOUS CASTING OF SPECIAL ALLOYS FOR CONSUMABLE ELECTRODES
    TUCHKEVICH, NM
    ALIPATOV, VI
    GRECHIN, VP
    [J]. STAL IN ENGLISH-USSR, 1970, (01): : 23 - +
  • [25] DEVELOPMENT OF A PROCESS FOR SEMI-CONTINUOUS CASTING OF ROLLING MILL ROLLS
    FILIPPOV, AS
    VETROV, BG
    KORNIENK.OA
    BELOUSOV, LA
    [J]. STAL IN ENGLISH-USSR, 1966, (07): : 580 - &
  • [26] A simplified design method for semi-continuous composite beams
    Department of Civil Engineering, Mostaganem University, Mostaganem, Algeria
    不详
    [J]. J. Appl. Sci., 2008, 24 (4533-4542):
  • [27] Formation mechanism of non-dendritic structure of aluminum alloy produced by semi-continuous casting of CREM process
    Zhang, Q.
    Lu, G.
    Cui, J.
    Zhang, B.
    [J]. Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (08): : 873 - 876
  • [28] Formation mechanism of non-dendritic structure of aluminum alloy produced by semi-continuous casting of CREM process
    Zhang, Q
    Lu, GM
    Cui, JZ
    Zhang, BJ
    [J]. ACTA METALLURGICA SINICA, 2001, 37 (08) : 873 - 876
  • [29] Bending and rotational behaviour of semi-continuous composite beams
    Wang, Jingfeng
    Li, Guoqiang
    [J]. FRONTIERS OF STRUCTURAL AND CIVIL ENGINEERING, 2008, 2 (02) : 116 - 122
  • [30] Composite frames with semi-continuous joints at the Millennium Tower
    Huber, Gerald
    Rubin, Daniel
    [J]. Stahlbau, 1999, 68 (08):
12345