Fatigue Durability of Ductile Iron in Very-High-Cycle Region

被引：0
|
作者：
Nový F. [1 ]
Kopas P. [1 ]
Bokuvka O. [1 ]
Savin A. [2 ]
机构：
[1] Faculty of Mechanical Engineering, University of Žilina, Univerzitná 1, Žilina
[2] National Institute of R&D for Technical Physics, Mangeron Boulevard 47, Iasi
来源：
Manufacturing Technology | 2016年 / 16卷 / 02期
关键词：
austempered ductile iron; Ductile iron; fatigue durability;
D O I：
10.21062/UJEP/X.2016/A/1213-2489/MT/16/2/406
中图分类号：
学科分类号：
摘要：
In this work there are published results about fatigue resistance of ductile iron with various types of matrix obtained at cyclic loading in very-high-cycle region. The results show continuous decrease of the stress amplitude with increasing of cycles number to the failure. The tensile strength increase is not accompanied with corresponding increase of fatigue properties. The fatigue durability decreases while the tensile strength increases. © 2016 Published by Manufacturing Technology. All Rights Reserved.
引用
收藏
页码：23 / 24
页数：1
相关论文
共 50 条
  • [41] Crack path and regularities for ball-bearing fracture in the very-high-cycle fatigue regime
    Shanyavskiy, Andrey A.
    Soldatenkov, Aleksey P.
    Fatigue and Fracture of Engineering Materials and Structures, 2022, 45 (11): : 3378 - 3392
  • [42] Very high cycle fatigue property of high-strength austempered ductile iron at conventional and ultrasonic frequency loading
    Zhang, Jiwang
    Song, Qingpeng
    Zhang, Ning
    Lu, Liantao
    Zhang, Mintang
    Cui, Guodong
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 70 : 235 - 240
  • [43] EFFECTS OF ENVIRONMENTAL MEDIA ON HIGH CYCLE AND VERY-HIGH-CYCLE FATIGUE BEHAVIORS OF STRUCTURAL STEEL 40Cr
    Qian Gui'an
    Hong Youshi
    ACTA METALLURGICA SINICA, 2009, 45 (11) : 1356 - 1363
  • [44] The Microscale Level of Ball-Bearing Ring Fracture in Very-High-Cycle Fatigue Regime
    Soldatenkov, A. P.
    Shanyavskiy, A. A.
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON PHYSICAL MESOMECHANICS. MATERIALS WITH MULTILEVEL HIERARCHICAL STRUCTURE AND INTELLIGENT MANUFACTURING TECHNOLOGY, 2020, 2310
  • [45] Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
    Hong, Youshi
    Lei, Zhengqiang
    Sun, Chengqi
    Zhao, Aiguo
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 58 : 144 - 151
  • [46] Microscopic damage evolution during very-high-cycle fatigue (VHCF) of tempered martensitic steel
    Krupp, U.
    Giertler, A.
    Koschella, K.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (11) : 1731 - 1740
  • [47] Application of Classical Fatigue and Fatigue-to-Fracture Techniques for Very-High-Cycle Life Qualification of Cardiac Devices
    Schmidt, Paul A.
    Krams, William E.
    Cao, Hengchu
    Jenkins, Timothy M.
    FOURTH SYMPOSIUM ON FATIGUE AND FRACTURE OF METALLIC MEDICAL MATERIALS AND DEVICES, 2019, 1616 : 148 - 163
  • [48] Very high cycle fatigue for single phase ductile materials: Comparison between α-iron, copper and α-brass polycrystals
    Favier, Veronique
    Blanche, Antoine
    Wang, Chong
    Ngoc Lam Phung
    Ranc, Nicolas
    Wagner, Daniele
    Bathias, Claude
    Chrysochoos, Andre
    Mughrabi, Hael
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 93 : 326 - 338
  • [49] Effects of strength level and loading frequency on very-high-cycle fatigue behavior for a bearing steel
    Zhao, Aiguo
    Xie, Jijia
    Sun, Chengqi
    Lei, Zhengqiang
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2012, 38 : 46 - 56
  • [50] Microstructural Influences on Very-High-Cycle Fatigue-Crack Initiation in Ti-6246
    C.J. Szczepanski
    S.K. Jha
    J.M. Larsen
    J.W. Jones
    Metallurgical and Materials Transactions A, 2008, 39 : 2841 - 2851
12345