Fatigue Durability of Ductile Iron in Very-High-Cycle Region

被引：0
|
作者：
Nový F. [1 ]
Kopas P. [1 ]
Bokuvka O. [1 ]
Savin A. [2 ]
机构：
[1] Faculty of Mechanical Engineering, University of Žilina, Univerzitná 1, Žilina
[2] National Institute of R&D for Technical Physics, Mangeron Boulevard 47, Iasi
来源：
Manufacturing Technology | 2016年 / 16卷 / 02期
关键词：
austempered ductile iron; Ductile iron; fatigue durability;
D O I：
10.21062/UJEP/X.2016/A/1213-2489/MT/16/2/406
中图分类号：
学科分类号：
摘要：
In this work there are published results about fatigue resistance of ductile iron with various types of matrix obtained at cyclic loading in very-high-cycle region. The results show continuous decrease of the stress amplitude with increasing of cycles number to the failure. The tensile strength increase is not accompanied with corresponding increase of fatigue properties. The fatigue durability decreases while the tensile strength increases. © 2016 Published by Manufacturing Technology. All Rights Reserved.
引用
收藏
页码：23 / 24
页数：1
相关论文
共 50 条
  • [31] ESSENTIAL CHARACTERISTICS AND INFLUENTIAL FACTORS FOR VERY-HIGH-CYCLE FATIGUE BEHAVIOR OF METALLIC MATERIALS
    Hong Youshi
    Zhao Aiguo
    Qian Gui'an
    ACTA METALLURGICA SINICA, 2009, 45 (07) : 769 - 780
  • [32] Pore-based prediction of crack initiation life in very-high-cycle fatigue
    Zhang, Ningyu
    Liu, Wenqi
    Shi, Tao
    Sun, Jingyu
    Qian, Guian
    International Journal of Fatigue, 2025, 190
  • [33] A general model for crack growth from initial defect in Very-High-Cycle Fatigue
    Paolino, Davide S.
    Tridello, Andrea
    Chiandussi, Giorgio
    Rossetto, Massimo
    XXIV ITALIAN GROUP OF FRACTURE CONFERENCE, 2017, 2017, 3 : 411 - 423
  • [34] Very-high-cycle fatigue behavior of a structural steel with and without induced surface defects
    Jiang, Qingqing
    Sun, Chengqi
    Liu, Xiaolong
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 93 : 352 - 362
  • [35] Effects of loading condition on very-high-cycle fatigue behaviour and dominant variable analysis
    Lei ZhengQiang
    Xie JiJia
    Sun ChengQi
    Hong YouShi
    SCIENCE CHINA-PHYSICS MECHANICS & ASTRONOMY, 2014, 57 (01) : 74 - 82
  • [36] A cumulative damage model for fatigue life estimation of high-strength steels in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Xie, J.
    Zhao, A.
    Lei, Z.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2012, 35 (07) : 638 - 647
  • [37] High-cycle fatigue of austempered ductile iron (ADI)
    Chapetti, Mirco D.
    INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (05) : 860 - 868
  • [38] Microstructure refinement and grain size distribution in crack initiation region of very-high-cycle fatigue regime for high-strength alloys
    Chang, Yukun
    Pan, Xiangnan
    Zheng, Liang
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134 (134)
  • [39] The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy
    Pan, Xiangnan
    Su, Hang
    Sun, Chengqi
    Hong, Youshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 115 : 67 - 78
  • [40] Effects of Loading Frequency and Loading Type on High-Cycle and Very-High-Cycle Fatigue of a High-Strength Steel
    Hu, Yuanpei
    Sun, Chengqi
    Xie, Jijia
    Hong, Youshi
    MATERIALS, 2018, 11 (08)
12345