Fatigue Durability of Ductile Iron in Very-High-Cycle Region

被引：0
|
作者：
Nový F. [1 ]
Kopas P. [1 ]
Bokuvka O. [1 ]
Savin A. [2 ]
机构：
[1] Faculty of Mechanical Engineering, University of Žilina, Univerzitná 1, Žilina
[2] National Institute of R&D for Technical Physics, Mangeron Boulevard 47, Iasi
来源：
Manufacturing Technology | 2016年 / 16卷 / 02期
关键词：
austempered ductile iron; Ductile iron; fatigue durability;
D O I：
10.21062/UJEP/X.2016/A/1213-2489/MT/16/2/406
中图分类号：
学科分类号：
摘要：
In this work there are published results about fatigue resistance of ductile iron with various types of matrix obtained at cyclic loading in very-high-cycle region. The results show continuous decrease of the stress amplitude with increasing of cycles number to the failure. The tensile strength increase is not accompanied with corresponding increase of fatigue properties. The fatigue durability decreases while the tensile strength increases. © 2016 Published by Manufacturing Technology. All Rights Reserved.
引用
收藏
页码：23 / 24
页数：1
相关论文
共 50 条
  • [1] Very High Cycle Fatigue of Two Ductile Iron Grades
    Bergstrom, Jens
    Burman, Christer
    Svensson, Jonas
    Jansson, Andreas
    Ivansson, Charlotta
    Zhou, Jing
    Valizadeh, Sima
    STEEL RESEARCH INTERNATIONAL, 2016, 87 (05) : 614 - 621
  • [2] FURTHER EXPLORATION ON CHARACTERISTIC REGION OF CRACK INITIATION FOR VERY-HIGH-CYCLE FATIGUE
    Hong Y.
    Lixue Xuebao/Chinese Journal of Theoretical and Applied Mechanics, 2022, 54 (08): : 2101 - 2118
  • [3] Multiaxial Fatigue Criteria and Durability of Titanium Compressor Disks in Low- and Very-high-cycle Fatigue Modes
    Burago, Nikolay
    Nikitin, Ilia
    MATHEMATICAL MODELING AND OPTIMIZATION OF COMPLEX STRUCTURES, 2016, 40 : 117 - 130
  • [4] The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels
    Hong, Youshi
    Liu, Xiaolong
    Lei, Zhengqiang
    Sun, Chengqi
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 89 : 108 - 118
  • [5] Propagation behaviour of microstructurally short fatigue cracks in the high-cycle- and very-high-cycle fatigue regimes
    Krupp, Ulrich
    Knobbe, Helge
    Dueber, Olaf
    Christ, Hans-Juergen
    Koester, Philipp
    Kuenkler, Boris
    Fritzen, Claus-Peter
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE V, 2008, 567-568 : 425 - +
  • [6] Fatigue of Austempered Ductile Iron with Two Strength Grades in Very High Cycle Regime
    Zhang, Jiwang
    Li, Wei
    Song, Qingpeng
    Zhang, Ning
    Lu, Liantao
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (03) : 744 - 749
  • [7] Fatigue of Austempered Ductile Iron with Two Strength Grades in Very High Cycle Regime
    Jiwang Zhang
    Wei Li
    Qingpeng Song
    Ning Zhang
    Liantao Lu
    Journal of Materials Engineering and Performance, 2016, 25 : 744 - 749
  • [8] Experimental investigation of Very-High-Cycle Fatigue behavior for a structural steel
    Qian, G. A.
    Hong, Y. S.
    ADVANCES IN HETEROGENEOUS MATERIAL MECHANICS 2008, 2008, : 1199 - 1202
  • [9] Effect of Aqueous Environment on High Cycle and Very-High-Cycle Fatigue Behavior for a Structural Steel
    Hong Youshi
    Qian Gui'an
    FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 355 - +
  • [10] Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Zhang, X.
    Liu, X.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (06) : 770 - 779
12345