Effect of Cr content on the microstructure evolution in weld metal for 1000 MPa grade high strength steel

被引：0
|
作者：
Feng, Wei [1 ]
Yu, Tingxiang [1 ,2 ]
Chen, Bo [1 ]
Zhang, Qingsu [1 ]
Cai, Hongguang [3 ]
Zhang, Biying [1 ]
Ma, Qiang [4 ]
机构：
[1] Harbin Well Welding Co., Ltd., Harbin,150060, China
[2] Harbin Welding Institute Limited Company, Harbin,150028, China
[3] Dalian Jinzhou Heavy Machinery Group Co., Ltd., Dalian,116100, China
[4] Jiangsu Rongda Material Corrosion Inspection Co., Ltd., Wuxi,214000, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2024年 / 45卷 / 09期
关键词：
Compendex;
D O I：
10.12073/j.hjxb.20240409001
中图分类号：
学科分类号：
摘要：
Ductile fracture
引用
收藏
页码：76 / 83
相关论文
共 50 条
  • [41] Microstructure and Mechanical Properties of GMAW Weld Metal of 890 MPa Class Steel
    Peng, Yun
    Peng, Xing-na
    Zhang, Xiao-mu
    Tian, Zhi-ling
    Wang, Tao
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2014, 21 (05) : 539 - 544
  • [42] Effect of interpass temperature on the microstructure and mechanical properties of multi-pass weld metal in a 550-MPa-grade offshore engineering steel
    X. L. Wang
    Y. T. Tsai
    J. R. Yang
    Z. Q. Wang
    X. C. Li
    C. J. Shang
    R. D. K. Misra
    Welding in the World, 2017, 61 : 1155 - 1168
  • [43] Effect of interpass temperature on the microstructure and mechanical properties of multi-pass weld metal in a 550-MPa-grade offshore engineering steel
    Wang, X. L.
    Tsai, Y. T.
    Yang, J. R.
    Wang, Z. Q.
    Li, X. C.
    Shang, C. J.
    Misra, R. D. K.
    WELDING IN THE WORLD, 2017, 61 (06) : 1155 - 1168
  • [44] Microstructure and Properties of High Strength Steel Weld Metals
    Gianetto, J. A.
    Goodall, G. R.
    Tyson, W. R.
    Fazeli, F.
    Quintana, M. A.
    Rajan, V. B.
    Chen, Y.
    PROCEEDINGS OF THE 9TH INTERNATIONAL PIPELINE CONFERENCE - 2012, VOL 3, 2013, : 515 - 526
  • [45] Effects of Welding Positions on Mechanical Properties and Microstructure in Weld Metal of High Strength Steel
    Masoumi, F.
    Shahriari, D.
    ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES, PTS 1 AND 2, 2010, 83-86 : 1121 - +
  • [46] Effect of chemical composition on microstructure and mechanical properties of laser weld metal of high-tensile-strength steel
    Sumi, Hiroyuki
    Oi, Kenji
    Yasuda, Koichi
    WELDING IN THE WORLD, 2015, 59 (02) : 173 - 178
  • [47] Effect of chemical composition on microstructure and mechanical properties of laser weld metal of high-tensile-strength steel
    Hiroyuki Sumi
    Kenji Oi
    Koichi Yasuda
    Welding in the World, 2015, 59 : 173 - 178
  • [48] Effect of aging temperature on the microstructure and mechanical properties of 1000MPa grade low carbon bainitic steel
    Zuo, Longfei
    Wei, Zhanlei
    Ni, Ri
    Ma, Ben
    Wang, Zidong
    MECHANICAL ENGINEERING AND MATERIALS, PTS 1-3, 2012, 152-154 : 376 - 380
  • [49] Effect of cooling rates after annealing on the microstructure and properties of 1000 MPa grade automobile steel for cold forming
    Dong, Ruifeng
    Zhao, Qingbo
    Bi, Xiaohong
    Deng, Xiangtao
    Shen, Wentian
    Lu, Yongfa
    Gele, Teri
    Baoxing
    MATERIALS RESEARCH EXPRESS, 2021, 8 (11)
  • [50] Effect of carbon on microstructure and properties of C-1.5Mn-2.5Ni-0.5Cr-0.5Mo high strength steel weld metal
    Qi, Yanchang
    Peng, Yun
    Wei, Jinshan
    Tian, Zhiling
    Hanjie Xuebao/Transactions of the China Welding Institution, 2010, 31 (11): : 41 - 44
12345