Effect of Cr content on the microstructure evolution in weld metal for 1000 MPa grade high strength steel

被引：0
|
作者：
Feng, Wei [1 ]
Yu, Tingxiang [1 ,2 ]
Chen, Bo [1 ]
Zhang, Qingsu [1 ]
Cai, Hongguang [3 ]
Zhang, Biying [1 ]
Ma, Qiang [4 ]
机构：
[1] Harbin Well Welding Co., Ltd., Harbin,150060, China
[2] Harbin Welding Institute Limited Company, Harbin,150028, China
[3] Dalian Jinzhou Heavy Machinery Group Co., Ltd., Dalian,116100, China
[4] Jiangsu Rongda Material Corrosion Inspection Co., Ltd., Wuxi,214000, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2024年 / 45卷 / 09期
关键词：
Compendex;
D O I：
10.12073/j.hjxb.20240409001
中图分类号：
学科分类号：
摘要：
Ductile fracture
引用
收藏
页码：76 / 83
相关论文
共 50 条
  • [31] Microstructure and mechanical properties of a novel 1000 MPa grade TMCP low carbon microalloyed steel with combination of high strength and excellent toughness
    Xie, Hui
    Du, Lin-Xiu
    Hu, Jun
    Misra, R. D. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 612 : 123 - 130
  • [32] Effect of Austenitizing Temperature on Microstructure and Crystallographic Evolution of 900 MPa Grade HSLA Steel
    Gao, Ye
    Ren, Jiakuan
    Li, Zhifeng
    Cui, Cong
    Chen, Jun
    Liu, Zhenyu
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2022, 36 (01): : 21 - 28
  • [33] Influence of cooling rate on microstructure and properties of high strength steel weld metal
    Keehan, E.
    Zachrisson, J.
    Karlsson, L.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2010, 15 (03) : 233 - 238
  • [34] Effect of Interpass Temperature on Microstructure and Mechanical Properties of Weld Metal of 690 MPa HSLA Steel
    Peng, Yun
    Wang, Aihua
    Xiao, Hongjun
    Tian, Zhilin
    THERMEC 2011, PTS 1-4, 2012, 706-709 : 2246 - 2252
  • [35] Influence of Nb Microalloying on the Microstructure and Toughness of 1000 MPa-Grade Deposited Weld Metals
    Zhao, Linlin
    An, Tongbang
    Zuo, Yue
    Cao, Zhilong
    Ma, Chengyong
    Kang, Ju
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
  • [36] Effect of Preheat Temperature and Microstructure on Cold Cracking in 600 MPa Grade Flux Cored Are Weld Metal
    Lee, Myungjin
    Cho, Kyungmox
    Kang, Namhyun
    KOREAN JOURNAL OF METALS AND MATERIALS, 2016, 54 (04): : 252 - 260
  • [37] Microstructure and Softening of Laser-Welded 960 MPa Grade High Strength Steel Joints
    Meng, Wei
    Li, Zhuguo
    Huang, Jian
    Wu, Yixiong
    Katayama, Seiji
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (02) : 538 - 544
  • [38] Microstructure and Softening of Laser-Welded 960 MPa Grade High Strength Steel Joints
    Wei Meng
    Zhuguo Li
    Jian Huang
    Yixiong Wu
    Seiji Katayama
    Journal of Materials Engineering and Performance, 2014, 23 : 538 - 544
  • [39] Modelling of microstructure evolution during hot rolling of a 780 MPa high strength steel
    Nakata, N
    Militzer, M
    ISIJ INTERNATIONAL, 2005, 45 (01) : 82 - 90
  • [40] Microstructure and Mechanical Properties of GMAW Weld Metal of 890 MPa Class Steel
    Yun Peng
    Xing-na Peng
    Xiao-mu Zhang
    Zhi-ling Tian
    Tao Wang
    Journal of Iron and Steel Research International, 2014, 21 : 539 - 544
12345