Stress-relief cracking susceptibility of a new ferritic steel - Part 1: Single-pass heat-affected zone simulations

被引：0

作者：

Nawrocki, J.G. ^{[1
]}

Dupont, J.N. ^{[1
]}

Robino, C.V. ^{[2
]}

Marder, A.R. ^{[1
]}

机构：

[1] Dept. of Mat. Sci. and Engineering, Lehigh University, Bethlehem, PA, United States

[2] Materials Joining Dept., Sandia National Laboratories, Albuquerque, NM, United States

来源：

Welding Journal (Miami, Fla) | 2000年 / 79卷 / 12期

关键词：

Crack initiation - Durability - Grain boundaries - Heat affected zone - Metallographic microstructure - Scanning electron microscopy - Stress analysis;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Heat affected zone (HAZ) simulation techniques were used to investigate the stress relief cracking (SRC) response of conventional steels. Postweld heat treatment (PWHT) and thermal simulations were used for the purpose. Optical and scanning electron microscopy (SEM) using thermal cycles were used to study microstructure of the coarse-grained heat-affected zone (CGHAZ).

引用

共 50 条

[1] The stres-relief cracking susceptibility of a new ferritic steel - part 2: Multiple-pass heat-affected zone Simulations
Nawrocki, JG
Dupont, JN
Robino, CV
Marder, AR
WELDING JOURNAL, 2001, 80 (01) : 18S - 24S
[2] Stress-relief cracking mechanism in simulated coarse-grained heat-affected zone of T23 steel
Li, Yong
Wang, Xue
Wang, Jiaqing
Chen, Ansheng
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2019, 266 : 73 - 81
[3] Influence of Boron on Stress-Relief Cracking Susceptibility of T23 Steel The effects of increasing boron content levels in the coarse grain heat-affected zone are analyzed
Zhang, D.
Wang, X.
WELDING JOURNAL, 2024, 103 (01) : 1S - 11S
[4] Susceptibility of Stress Relief Cracking in the Heat-Affected Zone of Low Alloy Creep Resistant Steels.
Holy, Miroslav
Koutnik, Milan
Schweissen und Schneiden/Welding and Cutting, 1978, 30 (02): : 53 - 57
[5] Sulfide stress cracking susceptibility of the heat-affected zone of an 9% Ni steel welded joint
Passos, Augusto Verissimo
Cipriano Farias, Francisco Werley
Pereira Moraes e Oliveira, Victor Hugo
Goncalves Rios, Mara Cardoso
Payao Filho, Joao da Cruz
CONSTRUCTION AND BUILDING MATERIALS, 2021, 282
[6] Sulfide stress cracking susceptibility of the heat-affected zone of an 9% Ni steel welded joint
Veríssimo Passos, Augusto
Farias, Francisco Werley Cipriano
Moraes e Oliveira, Victor Hugo Pereira
Rios, Mara Cardoso Gonçalves
Payão Filho, João da Cruz
Veríssimo Passos, Augusto (augusto.verissimo@poli.ufrj.br), 1600, Elsevier Ltd (282):
[7] Effect of High Temperature Ageing on Microstructure and Stress-Relief Cracking Susceptibility of Coarse Grain Heat Affected Zone in T23 steel
Wang Xue
Li Yong
Wang Jiaqing
Hu Lei
ACTA METALLURGICA SINICA, 2021, 57 (06) : 736 - 748
[8] PRECIPITATION SEQUENCES IN HEAT-AFFECTED ZONE OF 2-25CR-1-MO STEEL DURING STRESS-RELIEF HEAT-TREATMENT
HIPPSLEY, CA
METAL SCIENCE, 1981, 15 (04): : 137 - 147
[9] Heat-affected zone sensitization and stress corrosion cracking in 12% chromium type 1.4003 ferritic stainless steel
Du Toit, M.
Van Rooyen, G. T.
Smith, D.
CORROSION, 2007, 63 (05) : 395 - 404
[10] Reheating cracking susceptibility in the weld heat-affected zone of a reduced activation ferritic-martensitic steel for fusion reactors
Moon, Joonoh
Lee, Jin-Jong
Lee, Chang-Hoon
Park, Jun-Young
Lee, Tae-Ho
Cho, Kyung-Mox
Hong, Hyun-Uk
Kim, Hyoung Chan
FUSION ENGINEERING AND DESIGN, 2017, 124 : 1038 - 1041

← 1 2 3 4 5 →