Dissolution behavior of Al-Fe-Si alloys at NaOH etching treatment

被引：0
|
作者：
Seri, Osami [1 ]
Furumata, Kazunao [1 ]
Tagashira, Kohsuke [1 ]
机构：
[1] Muroran Inst of Technology, Hokkaido, Japan
来源：
Keikinzoku/Journal of Japan Institute of Light Metals | 1994年 / 44卷 / 06期
关键词：
Aluminum alloys - Caustic soda - Composition effects - Dissolution - Electrochemistry - Etching - Iron alloys - Reduction - Silicon alloys - Solutions;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Dissolution behavior of Al-Fe-Si alloys with various Fe/Si ratio have been investigated in a 5% NaOH solution. Weight loss of the alloys decreases with decreasing Fe/Si ratio in the alloys. Dissolution process under the NaOH etching treatment is controlled by the cathodic reaction of water reduction. It is electrochemically found that the intermetallic compounds with lower Fe/Si ratio in the Al-Fe-Si alloys cathodically plays poor role in the etching process.
引用
收藏
页码：315 / 319
相关论文
共 50 条
  • [41] Damage behaviours of various coarse Al-Fe-Si particles in model wrought alloys
    Toda, H
    Kobayashi, T
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 393 - 398
  • [42] Developing Al-Fe-Si alloys with high thermal stability through tuning Fe, Si contents and cooling rates
    Lan, Xinyue
    Li, Kai
    Wang, Jiong
    Yang, Mingjun
    Lu, Qiang
    Du, Yong
    INTERMETALLICS, 2022, 144
  • [43] Influence of DC and AC Magnetic Fields on the Solidification Structures of Al-Fe-Si Alloys
    Ban Chunyan
    Liu Na
    Wang Na
    Han Yi
    Ba Qixian
    Cui Jianzhong
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 : 102 - 106
  • [44] Influence of DC and AC Magnetic Fields on the Solidification Structures of Al-Fe-Si Alloys
    Ban Chunyan Liu Na Wang Na Han Yi Ba Qixian Cui Jianzhong Key Laboratory of National Education Ministry for Electromagnetic Processing of Materials Northeastern University Shenyang China
    稀有金属材料与工程, 2011, 40(S3) (S3) : 102 - 106
  • [45] Phase transformation during annealing of rapidly solidified Al-Rich Al-Fe-Si alloys
    Bendersky, L.A.
    McAlister, A.J.
    Biancaniello, F.S.
    Metallurgical transactions. A, Physical metallurgy and materials science, 1988, 19 A (12): : 2893 - 2900
  • [46] Assessment of the Al corner of the ternary Al-Fe-Si system
    Eleno, Luiz
    Vezely, Josef
    Sundman, Bo
    Cieslar, Miroslav
    Lacaze, Jacques
    SOLIDIFICATION AND GRAVITY V, 2010, 649 : 523 - +
  • [47] Downstream processing of some Al-Fe-Mn-Si and Al-Fe-Si TRC alloys and its influence on sheet/foil properties
    Delijic, K.
    Asanovic, V.
    Radonjic, D.
    RECENT DEVELOPMENTS IN ADVANCED MATERIALS AND PROCESSES, 2006, 518 : 543 - 548
  • [48] Update of Al-Fe-Si, Al-Mn-Si and Al-Fe-Mn-Si thermodynamic descriptions
    Chen, Hai-lin
    Chen, Qing
    Du, Yong
    Bratberg, Johan
    Engstrom, Anders
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (07) : 2041 - 2053
  • [49] Al-Fe-Si (Aluminum-Iron-Silicon)
    Raghavan, V.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2012, 33 (04) : 322 - 326
  • [50] MICROPROBE ANALYSIS OF THE AL-FE-SI VARIATION IN LATERITES
    SCHELLMANN, W
    CHEMIE DER ERDE-GEOCHEMISTRY, 1995, 55 (02) : 97 - 108
12345