Dissolution behavior of Al-Fe-Si alloys at NaOH etching treatment

被引：0
|
作者：
Seri, Osami [1 ]
Furumata, Kazunao [1 ]
Tagashira, Kohsuke [1 ]
机构：
[1] Muroran Inst of Technology, Hokkaido, Japan
来源：
Keikinzoku/Journal of Japan Institute of Light Metals | 1994年 / 44卷 / 06期
关键词：
Aluminum alloys - Caustic soda - Composition effects - Dissolution - Electrochemistry - Etching - Iron alloys - Reduction - Silicon alloys - Solutions;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Dissolution behavior of Al-Fe-Si alloys with various Fe/Si ratio have been investigated in a 5% NaOH solution. Weight loss of the alloys decreases with decreasing Fe/Si ratio in the alloys. Dissolution process under the NaOH etching treatment is controlled by the cathodic reaction of water reduction. It is electrochemically found that the intermetallic compounds with lower Fe/Si ratio in the Al-Fe-Si alloys cathodically plays poor role in the etching process.
引用
收藏
页码：315 / 319
相关论文
共 50 条
  • [21] STRUCTURAL STUDY OF LIQUID AND AS-QUENCHED Al-Fe-Si ALLOYS
    Muratov, O. S.
    Kazimirov, V. P.
    Roik, O. S.
    Yakovenko, O. M.
    Sokolskii, V. E.
    Mika, T. M.
    Kashirina, Ya O.
    Galushko, S. M.
    JOURNAL OF PHYSICAL STUDIES, 2019, 23 (04):
  • [22] INFLUENCE OF HOMOGENIZING HEAT-TREATMENT ON HOT DEFORMATIONS OF ALUMINUM AND AL-FE-SI ALLOYS
    USUI, E
    INABA, T
    SHINANO, N
    ZEITSCHRIFT FUR METALLKUNDE, 1985, 76 (12): : 786 - 791
  • [23] DETERMINATION OF THE STRUCTURE OF INTERCELLULAR PRECIPITATES IN RAPIDLY SOLIDIFIED AL-FE ALLOYS BY COMPARISON WITH AL-FE-SI ALLOYS
    CARRARD, M
    GREMAUD, M
    PIERANTONI, M
    SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (04): : 925 - 930
  • [24] Effect of Iron and Silicon Content on the Hot Compressive Deformation Behavior of Dilute Al-Fe-Si Alloys
    Shakiba, M.
    Parson, N.
    Chen, X. -G.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (01) : 404 - 415
  • [25] Equilibrium and non-equilibrium intermetallic phases in Al-Fe and Al-Fe-Si alloys
    Griger, A
    Stefaniay, V
    JOURNAL OF MATERIALS SCIENCE, 1996, 31 (24) : 6645 - 6652
  • [26] Effect of Iron and Silicon Content on the Hot Compressive Deformation Behavior of Dilute Al-Fe-Si Alloys
    M. Shakiba
    N. Parson
    X.-G. Chen
    Journal of Materials Engineering and Performance, 2015, 24 : 404 - 415
  • [27] Effect of homogenization treatment and silicon content on the microstructure and hot workability of dilute Al-Fe-Si alloys
    Shakiba, M.
    Parson, N.
    Chen, X. -G.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 619 : 180 - 189
  • [28] Effect of casting and homogenizing treatment conditions on the formation of Al-Fe-Si intermetallic compounds in 6063 Al-Mg-Si alloys
    Tanihata, H
    Sugawara, T
    Matsuda, K
    Ikeno, S
    JOURNAL OF MATERIALS SCIENCE, 1999, 34 (06) : 1205 - 1210
  • [29] Enthalpy of formation of Al-Fe-Si alloys (τ5,τ10,τ1,τ9)
    Li, Y
    Ochin, P
    Quivy, A
    Telolahy, P
    Legendre, B
    JOURNAL OF ALLOYS AND COMPOUNDS, 2000, 298 (1-2) : 198 - 202
  • [30] Intermetallic phase selection during solidification of Al-Fe-Si(-Mg) alloys
    Meredith, MW
    Worth, J
    Hamerton, RG
    ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 : 107 - 112
12345