EFFECT OF STRAIN RATE ON CORROSION OF SOME SHEET METALS.

被引：0
|
作者：
Behera, T. [1 ]
机构：
[1] Regional Engineering Coll, Rourkela, India, Regional Engineering Coll, Rourkela, India
来源：
Journal of the Institution of Engineers (India): Chemical Engineering Division | 1984年 / 65卷
关键词：
CORROSION - Measurements - HEAT TREATMENT - Annealing - METAL FORMING - Explosive;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Investigations have been carried out to evalaute the corrosion rates of hydraulically bulged and explosively formed products deformed to failure and as annealed sheets of 0. 11%C steel, 65 : 35 brass, commercial copper and aluminum in sodium chloride medium. A hydraulic bulge testing apparatus has been designed and developed for deforming blanks of thin sheets under balanced biaxial loading at a low strain rate. The corrosion rate of hydraulicaly bulged specimens have intermediate range of values, higher than the as-annealed materials but lower than the explosively formed products. The results are comparable with the data reported by other investigators. It is concluded that the corrosion susceptibility of these materials is markedly increased with the strain rate of cold working. It is recommended that this enhancement of corrosion susceptibility of the products can be economically eliminated by normalizing.
引用
收藏
页码：7 / 10
相关论文
共 50 条
  • [41] CRITICAL SURVEY OF DATA SOURCES: CORROSION OF METALS.
    Diegle, Ronald B.
    Boyd, Walter K.
    National Bureau of Standards, Special Publication, 1976, (396-3):
  • [42] ON THE NATURE OF CORROSION-MECHANICAL WEAR OF METALS.
    Preis, G.A.
    Soviet Journal of Friction and Wear (English translation of Trenie i Iznos), 1987, 8 (05): : 16 - 20
  • [43] Third Report to the Corrosion Committee of the Institute of Metals.
    Gibbs, WE
    Smith, RH
    Bengough, GD
    JOURNAL OF THE INSTITUTE OF METALS, 1916, 15 : 37 - 183
  • [44] GUIDELINES FOR CORROSION TESTING OF COATED AND UNCOATED METALS.
    El-Sawy, S.M.
    Anti-Corrosion Methods and Materials, 1985, 32 (11) : 16 - 18
  • [45] Identification of Plastic Behaviour of Sheet Metals in High Strain Rate Tests
    Amodio, D.
    Mancini, E.
    Rossi, M.
    Sasso, M.
    CHALLENGES IN MECHANICS OF TIME DEPENDENT MATERIALS, VOL 2, 2017, : 203 - 209
  • [46] Strain-rate-dependent forming limit diagrams for sheet metals
    Gerdooei, M.
    Dariani, B. M.
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 2008, 222 (12) : 1651 - 1659
  • [47] Forming limit diagrams of strain-rate-dependent sheet metals
    Jie, M.
    Cheng, C. H.
    Chan, L. C.
    Chow, C. L.
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2009, 51 (04) : 269 - 275
  • [48] SOME RESULTS ON PLASTIC DEFORMABILITY ON METALS.
    Matsuura, Yuji
    Morimoto, Hideo
    Report of the Castings Research Laboratory, Waseda University, 1980, (31): : 1 - 11
  • [49] The latent heat of fusion of some metals.
    Awbery, JH
    Griffiths, E
    PROCEEDINGS OF THE PHYSICAL SOCIETY, 1926, 38 : 378 - 398
  • [50] EFFECT OF DELTA FERRITE CONTENT ON THE CORROSION RESISTANCE OF TYPE 316 CLAD METALS.
    Prasad Rao, K.
    Maheshwar Rao, A.Uma
    Gururaja, G.J.
    Werkstoffe und Korrosion, 1988, 39 (03): : 135 - 142
12345