EFFECT OF STRAIN RATE ON CORROSION OF SOME SHEET METALS.

被引：0
|
作者：
Behera, T. [1 ]
机构：
[1] Regional Engineering Coll, Rourkela, India, Regional Engineering Coll, Rourkela, India
来源：
Journal of the Institution of Engineers (India): Chemical Engineering Division | 1984年 / 65卷
关键词：
CORROSION - Measurements - HEAT TREATMENT - Annealing - METAL FORMING - Explosive;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Investigations have been carried out to evalaute the corrosion rates of hydraulically bulged and explosively formed products deformed to failure and as annealed sheets of 0. 11%C steel, 65 : 35 brass, commercial copper and aluminum in sodium chloride medium. A hydraulic bulge testing apparatus has been designed and developed for deforming blanks of thin sheets under balanced biaxial loading at a low strain rate. The corrosion rate of hydraulicaly bulged specimens have intermediate range of values, higher than the as-annealed materials but lower than the explosively formed products. The results are comparable with the data reported by other investigators. It is concluded that the corrosion susceptibility of these materials is markedly increased with the strain rate of cold working. It is recommended that this enhancement of corrosion susceptibility of the products can be economically eliminated by normalizing.
引用
收藏
页码：7 / 10
相关论文
共 50 条
  • [31] GENERALIZED QUADRATIC FLOW LAW FOR SHEET METALS.
    Jones, S.E.
    Gillis, P.P.
    1600, (15 A):
  • [32] Bacterial corrosion of metals. II. Gravimetric investigations of the corrosion of nonferrous metals
    Gerasimenko, AA
    Matyusha, GV
    PROTECTION OF METALS, 2000, 36 (03): : 279 - 284
  • [33] Bacterial corrosion of metals. II. Gravimetric investigations of the corrosion of nonferrous metals
    A. A. Gerasimenko
    G. V. Matyusha
    Protection of Metals, 2000, 36 : 279 - 284
  • [34] Comments on the strain hardening and annealing of metals.
    Guillet, L
    Cournot, J
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES, 1930, 190 : 905 - 908
  • [35] STRAIN FIELDS ASSOCIATED WITH THE INDENTATION OF METALS.
    Woodward, R.L.
    Journal of the Australian Institute of Metals, 1974, 19 (02): : 128 - 135
  • [36] The oligodynamic effect of metals.
    Acel, D
    BIOCHEMISCHE ZEITSCHRIFT, 1920, 112 : 23 - 26
  • [37] EFFECT OF STRAIN-RATE SENSITIVITY OF FLOW-STRESS ON STRETCH FORMABILITY OF SHEET METALS
    CONRAD, H
    JOURNAL OF MECHANICAL WORKING TECHNOLOGY, 1978, 2 (01): : 67 - 74
  • [38] Corrosion and Highly Wear Resistant Hard Metals.
    Kny, Erich
    Bader, Tobias
    Hohenrainer, Christa
    Schmid, Lothar
    Werkstoffe und Korrosion, 1986, 37 (05): : 230 - 235
  • [39] Fourth report to the corrosion committee of the Institute of Metals.
    Bengough, GD
    JOURNAL OF THE INSTITUTE OF METALS, 1919, 21 : 37 - 252
  • [40] CORROSION CRACKING OF METALS AT CONSTANT STRESS AND CONSTANT STRAIN RATE
    NIKITIN, VI
    SOVIET MATERIALS SCIENCE, 1989, 25 (01): : 26 - 32
12345