Influence of Microstructure on Fatigue Crack Propagation Rate of Aluminum Alloys.

被引：0
|
作者：
Albrecht, Joachim
Luetjering, Gerd
机构：
来源：
Deutsche Luft- und Raumfahrt, Forschungsbericht | 1977年 / 77-7期
关键词：
D O I：
暂无
中图分类号：
TG146.2+1 [铝]; TF821 [铝];
学科分类号：
摘要：
The influence of microstructure on fatigue crack propagation rate was investigated for three different AlZnMgCu-alloys with similar tensile properties. Tests were performed under vacuum and in laboratory air to estimate the influence of environment. A pronounced influence of microstructure on crack propagation rate was found for fatigue under vacuum as well as in air. Crack propagation along slip bands in a high-purity underaged alloy exhibited the slowest, crack propagation by void coalescence in commercial alloys the highest crack propagation rate.
引用
下载
收藏
相关论文
共 50 条
  • [21] THE INFLUENCE OF MICROSTRUCTURE ON FATIGUE CRACK-PROPAGATION IN POLYOXYMETHYLENE
    RUNT, J
    GALLAGHER, KP
    JOURNAL OF MATERIALS SCIENCE, 1991, 26 (03) : 792 - 798
  • [22] EFFECT OF THE STABILITY OF A SOLID-SOLUTION OF ALUMINUM-ALLOYS ON THE RATE OF PROPAGATION OF A FATIGUE CRACK
    GUREVICH, SE
    NAMDAKOV, DZ
    RUSSIAN METALLURGY, 1990, (06): : 118 - 123
  • [23] Prediction of corrosion fatigue crack growth rate in alloys. Part I: General corrosion fatigue model for aero-space aluminum alloys
    Koyalov, Danyil
    Fekete, Balazs
    Engelhardt, George R.
    Macdonald, Digby D.
    CORROSION SCIENCE, 2018, 141 : 22 - 29
  • [24] Environmental influence on fatigue crack propagation in TiAl alloys
    Mabru, C
    Henaff, G
    Petit, J
    INTERMETALLICS, 1997, 5 (05) : 355 - 360
  • [25] Influence of Temperature on Fatigue Crack Propagation in TiAl Alloys*
    R. C. Feng
    Z. Y. Rui
    Y. Zuo
    C. F. Yan
    G. T. Zhang
    Strength of Materials, 2014, 46 : 417 - 421
  • [26] Influence of Temperature on Fatigue Crack Propagation in TiAl Alloys*
    Feng, R. C.
    Rui, Z. Y.
    Zuo, Y.
    Yan, C. F.
    Zhang, G. T.
    STRENGTH OF MATERIALS, 2014, 46 (03) : 417 - 421
  • [27] INFLUENCE OF LOADING FREQUENCY ON THE RATE OF FATIGUE CRACK-GROWTH IN ALUMINUM-ALLOYS
    STAROVA, EN
    INDUSTRIAL LABORATORY, 1980, 46 (07): : 732 - 734
  • [28] Crack Propagation and Residual Static Strength of New High Strength Aluminum Alloys.
    Schuetz, W.
    Oberparleiter, W.
    1600, (48):
  • [29] K1* - N DIAGRAM OF FATIGUE CRACK RESISTANCE OF ALUMINUM ALLOYS.
    Ivanova, V.S.
    Kunavin, S.A.
    Russian metallurgy. Metally, 1984, (04) : 156 - 162
  • [30] INFLUENCE OF MICROSTRUCTURE, ENVIRONMENT AND TEMPERATURE ON FATIGUE CRACK PROPAGATION IN 2XXX ALUMINIUM ALLOYS
    Petit, Jean
    Sarrazin-Baudoux, Christine
    Gerland, Michel
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE VII, 2014, 592-593 : 22 - 29
12345