Fabrication and characterization of high quality NdBa2Cu3O7-δ/Sr2AlTaO6/ NdBa2Cu3O7-δ and NdBa2Cu3O7-δ/Sr2AlNbO6/ NdBa2Cu3O7-δ multilayers

被引：0
|
作者：
Int Superconductivity Technology, Cent, Tokyo, Japan [1 ]
机构：
来源：
IEEE Trans Appl Supercond | / 2 III卷 / 3460-3463期
关键词：
In high-T; superconducting multilayer structures including superconductor; insulator; and barrier layers; lattice matched insulators with a low dielectric constant E; and a low value of loss tangent tan6 are needed. It is well known that the superconductivity in a cuprate system is very sensitive to the structure; impurities; and oxygen content. In order to fabricate Josephson junctions with high performance for high-speed operation of superconducting circuits; the essential prerequisite is the all-epitaxial structure; smooth surface; and abrupt interface. A number of issues are critical in the insulator layer selection for applications. Besides the consideration of lattice match; chemical compatibility; the difference of thermal expansion coefficients; and dielectric properties; a favorable insulator should also have a sufficiently high oxygen diffusion rate at about 450 OC; permitting oxygen to diffuse through it and into the underlying high-T; layer; Recently; many kinds of substrate materials for growth of YBa2Cu307.g (YBCO) films have been deposited as insulator layers in multilayer structures; such as SrTi03; Manuscript received September 15; 1998. This work was supported by the New Energy and Industrial Technology Development Organization (NEDO) for the R & D of Industrial Science and Technology Frontier Program through International Superconductivity Technology Center (ISTEC);
D O I：
暂无
中图分类号：
学科分类号：
摘要：
11
引用
收藏
相关论文
共 50 条
  • [21] Instability of the critical state in NdBa2Cu3O7-δ single crystals
    Koblischka, MR
    Murakami, M
    Johansen, TH
    Baziljevich, M
    Frello, T
    Wolf, T
    PHYSICA STATUS SOLIDI B-BASIC RESEARCH, 1999, 215 (02): : R11 - R12
  • [22] Scaling of current densities and pinning forces in NdBa2CU3O7-δ
    Koblischka, MR
    van Dalen, AJJ
    Higuchi, T
    Sawada, K
    Kojo, H
    Yoo, SI
    Murakami, M
    APPLIED SUPERCONDUCTIVITY 1997, VOLS 1 AND 2: VOL 1: SMALL SCALE AND ELECTRONIC APPLICATIONS; VOL 2: LARGE SCALE AND POWER APPLICATIONS, 1997, (158): : 1145 - 1148
  • [23] Fabrication and characterization of BaSnO3-doped NdBa2Cu3O7-δ thin film
    Tanaka, Y.
    Mukaida, M.
    Teranishi, R.
    Yamada, K.
    Ichinose, A.
    Matsumoto, K.
    Horii, S.
    Yoshida, Y.
    Kita, R.
    Fujiyoshi, T.
    Mori, N.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2008, 468 (15-20): : 1864 - 1868
  • [24] (110) NdBa2CU3O7-δ and YBa2CU3O7-δ films grown on (110) NdBa2Cu3O7-δ single crystal substrates by 90° off-axis RF magnetron sputtering methods
    Usagawa, T
    Yao, X
    Koyama, S
    Tanabe, K
    Izumi, T
    Shiohara, Y
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2001, 40 (8A): : L792 - L795
  • [25] Theoretical investigations of the EPR g factors for tetragonal NdBa2Cu3O7-δ
    Wu, SY
    Dong, HN
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (12): : 1430 - 1433
  • [26] Carrier concentration induced transformations and existence of pseudogap in NdBa2Cu3O7-δ
    Mollah, S.
    Biswas, B.
    Haldar, S.
    Ghosh, Ajay Kumar
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2017, 539 : 40 - 43
  • [27] Effects of substrates on the NdBa2Cu3O7-δ films fabricated by the PLD process
    Wee, SH
    Moon, SH
    Park, C
    Yoo, SI
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 996 - 1000
  • [28] NdBa2Cu3O7-δ superconducting thin films made by the PLD method
    Moon, Seung-Hyun
    Oh, Byungdu
    Physica C: Superconductivity and its Applications, 1997, 282-287 (pt 2): : 677 - 678
  • [29] Smooth NdBa2Cu3O7-δ thin films and ramp Josephson junctions
    Sjostrand, M.
    Komissinski, P.
    Winkler, D.
    7TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'05), 2006, 43 : 1139 - 1142
  • [30] C-axis quasiparticle tunneling properties of planar NdBa2Cu3O7-δ/ PrBa2Cu3O7-δ /NdBa 2Cu3O7-δ quasi-homostructures
    Alvarez, G.A.
    Utagawa, T.
    Enomoto, Y.
    Physica C: Superconductivity and its Applications, 1997, 282-287 (pt 3): : 1483 - 1484
12345