Corrosion behavior of zinc chromate coatings

被引：0
|
作者：
Martyak, Nicholas M. [1 ]
McCaskie, J.E. [1 ]
Harrison, Lew [1 ]
机构：
[1] Atotech USA Inc, Somerset, United States
来源：
Metal Finishing | 1996年 / 94卷 / 02期
关键词：
Anodic polarization - Atomic force microscopy - Corrosion resistance - Crack propagation - Cracks - Current density - Electrochemical corrosion - Optical microscopy - Protective coatings - Surface structure - Zinc compounds;
D O I：
10.1016/S0026-0576(96)93872-6
中图分类号：
学科分类号：
摘要：
The corrosion protection offered by chromated zinc deposits was electrochemically studied. The surface structures of the zinc and chromate coatings were studied using optical and atomic force microscopy (AFM). Corrosion performance was studied in situ and the protective nature of the different chromate layers were determined. Unprotected zinc quickly corroded in a chloride medium. Black, green, and yellow chromate films increased the corrosion protection. The corrosion protection of chromated zinc coatings was qualitatively ranked using galvanostatic methods. Corrosion in black, green, and yellow chromate films was observed to start and propagate along cracks within the chromate coatings. Blue chromate films exhibited generalized corrosion.
引用
收藏
页码：65 / 67
相关论文
共 50 条
  • [21] Corrosion behavior of electrodeposited tin-zinc alloy coatings on steel
    Pickering, H.W. (pick@ems.psu.edu), 2005, American Electroplaters and Surface Finishers Soc. Inc. (92):
  • [22] CHROMATE ION INHIBITION OF THE DIFFERENTIAL OXYGEN CORROSION OF ZINC
    WRIGHT, MM
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1962, 109 (08) : C200 - C200
  • [23] Electrochemical corrosion behavior of nanocrystalline zinc coatings in 3.5% NaCl solutions
    Li, Mou Cheng
    Jiang, Li Li
    Zhang, Wen Qi
    Qian, Yu Hai
    Luo, Su Zhen
    Shen, Jia Nian
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2007, 11 (09) : 1319 - 1325
  • [24] The Corrosion Behavior of Cold Sprayed Zinc Coatings on Mild Steel Substrate
    Chavan, Naveen Manhar
    Kiran, B.
    Jyothirmayi, A.
    Phani, P. Sudharshan
    Sundararajan, G.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2013, 22 (04) : 463 - 470
  • [25] THE FORMATION, STRUCTURE AND CORROSION BEHAVIOR OF CONVERSION COATINGS ON ZINC ALLOY ELECTRODEPOSITS
    ABIBSI, A
    SHORT, NR
    DENNIS, JK
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1991, 69 : 45 - 49
  • [26] CHARACTERIZATION OF THE CORROSION BEHAVIOR OF ZINC-ALUMINUM THERMAL SPRAY COATINGS
    SHAW, BA
    MORAN, PJ
    MATERIALS PERFORMANCE, 1985, 24 (11) : 22 - 31
  • [27] The Corrosion Behavior of Cold Sprayed Zinc Coatings on Mild Steel Substrate
    Naveen Manhar Chavan
    B Kiran
    A Jyothirmayi
    P Sudharshan Phani
    G Sundararajan
    Journal of Thermal Spray Technology, 2013, 22 : 463 - 470
  • [28] Corrosion behavior of electrodeposited tin-zinc alloy coatings on steel
    Maurer, E
    Pickering, HW
    Weil, K
    PLATING AND SURFACE FINISHING, 2005, 92 (06): : 32 - 36
  • [29] Active corrosion protection and corrosion sensing in chromate-free organic coatings
    Buchheit, RG
    Guan, H
    Mahajanam, S
    Wong, F
    PROGRESS IN ORGANIC COATINGS, 2003, 47 (3-4) : 174 - 182
  • [30] Morphology and Corrosion Performance of Chromate Conversion Coatings on Different Substrates
    Antonio Dominguez-Crespo, Miguel
    Onofre-Bustamante, Edgar
    Minerva Torres-Huerta, Aide
    Rodriguez-Gomez, Francisco J.
    JOURNAL OF THE MEXICAN CHEMICAL SOCIETY, 2008, 52 (04) : 235 - 240
12345