REVIEW OF THE CRYSTALLOGRAPHY OF STRESS CORROSION CRACKING.

被引：0
|
作者：
Meletis, E.I. [1 ]
Hochman, R.F. [1 ]
机构：
[1] IIT Research Inst, Chicago, IL, USA, IIT Research Inst, Chicago, IL, USA
来源：
Corrosion Science | 1986年 / 26卷 / 01期
关键词：
BRITTLE FAILURE - CORRODENTS - CRACK PROPAGATION - DUCTILITY - HYDROGEN-ASSISTED FRACTURE;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
(Edited Abstract)
引用
收藏
页码：63 / 90
相关论文
共 50 条
  • [31] Stress corrosion cracking of magnesium alloys: A review
    Jiahao Jiang
    Xue Geng
    Xiaobo Zhang
    Journal of Magnesium and Alloys, 2023, 11 (06) : 1906 - 1930
  • [32] Stress corrosion cracking of magnesium alloys: A review
    Jiang, Jiahao
    Geng, Xue
    Zhang, Xiaobo
    JOURNAL OF MAGNESIUM AND ALLOYS, 2023, 11 (06) : 1906 - 1930
  • [33] Fire Cracking.
    Form, W.
    Peguiron, N.
    Furrer, B.
    Memoires et etudes scientifiques de la Revue de metallurgie, 1982, 79 (03): : 143 - 148
  • [34] HEAT TREATMENT TO REDUCE THE SUSCEPTIBILITY OF Al-Zn-Mg-Cu ALLOY TO STRESS CORROSION CRACKING.
    Ohnishi, Tadakazu
    Shiota, Hideaki
    Keikinzoku/Journal of Japan Institute of Light Metals, 1986, 36 (10): : 647 - 656
  • [35] ENVIRONMENTALLY ENHANCED FATIGUE CRACK GROWTH OF A HIGH-STRENGTH STEEL SENSITIVE TO STRESS CORROSION CRACKING.
    Endo, Kichiro
    Komai, Kenjiro
    Fujimoto, Tomoji
    Matsuda, Yoshinobu
    Bulletin of the JSME, 1980, 23 (180): : 807 - 814
  • [36] CRYSTALLOGRAPHY AND KINETICS OF STRESS CORROSION CRACKING IN TYPE 3116 STAINLESS STEEL SINGLE CRYSTALS
    MAREK, M
    HOCHMAN, RF
    CORROSION, 1971, 27 (09) : 361 - &
  • [37] ROLLFORMING WITHOUT CRACKING.
    Quinchon, Guy
    Sheet Metal Industries, 1984, 61 (05): : 277 - 278
  • [38] CHEMISTRY OF CATALYTIC CRACKING.
    Corma, A.
    Wojciechowski, B.W.
    Catalysis reviews, 1985, 27 (01): : 29 - 150
  • [39] EFFECT OF AGING PROCESSES ON THE RESISTANCE OF ALUMINUM ALLOY 1201 TO CORROSION CRACKING.
    Sinyavskii, V.S.
    Sorokina, V.P.
    Lebedeva, I.G.
    Protection of Metals, 1975, 11 (01): : 11 - 15
  • [40] INFLUENCE OF ARSENIC, ANTIMONY, AND BISMUTH ON THE SUSCEPTIBILITY OF AUSTENITIC ALLOYS TO CORROSION CRACKING.
    Ryabchenkov, A.V.
    Gerasimov, V.I.
    Aksenova, L.I.
    Hubner, V.
    Rosborg, Bo
    Protection of Metals (English translation of Zaschita Metallov), 1980, 16 (03): : 214 - 220
12345