Influence of Ag substrates on grain alignment and critical current density of Bi-2212 tape conductors

被引：0

作者：

Kumakura, H. ^{[1
]}

Kitaguchi, H. ^{[1
]}

Togano, K. ^{[1
]}

Muroga, T. ^{[1
]}

Sato, J. ^{[1
]}

Okada, M. ^{[1
]}

机构：

[1] Natl Research Inst for Metals, Ibaraki, Japan

来源：

IEEE Transactions on Applied Superconductivity | 1999年 / 9卷 / 2 II期

关键词：

Bismuth compounds - Coating techniques - Critical current density (superconductivity) - Crystal impurities - Crystal microstructure - Interfaces (materials) - Silver - Superconducting films - Surface roughness - Tapes - X ray diffraction;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

We investigated the influence of Ag substrate on the microstructure and Jc values of dip-coated Bi-2212/Ag tapes. The grain alignment of Bi-2212 in the oxide/Ag interface was much higher than that in the free surface of oxide. Jc increases with increasing oxide/Ag interface area and with decreasing oxide layer thickness, while Jc was almost independent of the free surface area. The smoothness of the Ag substrate is also an important factor. Micrometer-size roughness of the Ag substrate results in a decrease of Bi-2212 grain alignment and therefore Jc. Addition of alloying elements to the Ag also degrades the grain alignment of Bi-2212 and decreased Jc. Cold rolling before the heat treatment improved the grain alignment and enhanced Jc.

引用

页码：1804 / 1807

共 50 条

[21] The influence of critical current density of Bi-2212 superconductors by defects after Yb-doping
Lu, Tianni
Zhang, Cuiping
Guo, Shengwu
Wu, Yifang
Li, Chengshan
Zhou, Lian
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2015, 519 : 24 - 27
[22] Development of large current capacity Bi-2212 monolithic conductors
Koizumi, T
Nakatsu, T
Ohtani, N
Aoki, Y
Hasegawa, T
Hirano, N
Nagaya, S
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 392 : 1025 - 1029
[23] Current-voltage curves of a Bi-2212/Ag multilayered tape prepared by PAIR process
Yamasaki, A
Ueno, Y
Kiuchi, M
Matsushita, T
Miao, HP
Kumakura, H
Kitaguchi, H
ADVANCES IN SUPERCONDUCTIVITY XII, 2000, : 407 - 409
[24] Making strain effects inside Bi-2212/Ag conductors visible
Trociewitz, Ulf Peter
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2015, 28 (07):
[25] Critical current density at low temperatures in Bi-2212 superconductor with small anisotropy
Haraguchi, T
Imada, T
Kiuchi, M
Otabe, ES
Matsushita, T
Yasuda, T
Okayasu, S
Uchida, S
Shimoyama, J
Kishio, K
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 304 - 308
[26] Control of partially melted microstructure and critical current density for Bi-2212 tapes
Funahashi, R.
Matsubara, I.
Ueno, H.
Ishikawa, H.
Physica C: Superconductivity and its Applications, 1997, 282-287 (pt 4): : 2579 - 2580
[27] Effect of Ca Content on the Critical Current Density and Flux Pinning Properties of Ag sheathed Bi-2212 tapes
Li, Chengshan
Zhang, Shengnan
Hao, Qingbin
Zhang, Yilei
Zhang, Pingxiang
SUPERCONDUCTIVITY CENTENNIAL CONFERENCE 2011, 2012, 36 : 1599 - 1604
[28] Critical current density of Bi-2212 thick films processed by partial melting
Buhl, D
Lang, T
Gauckler, LJ
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1997, 10 (01): : 32 - 40
[29] Effects of Rolling Reduction on Critical Current Density and Microstructure of Bi-2212 Wires
Jiang, Jianyi
Kvitkovic, Jozef
Linville, Caitlynn
Brown, Jamia
Jones, Jakeyvan
Davis, Daniel S.
Kim, Youngjae
Kametani, Fumitake
Trociewitz, Ulf P.
Hellstrom, Eric E.
Larbalestier, David C.
Croteau, Jean-Francois
Escobar, Christopher
Shen, Tengming
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2025, 35 (05)
[30] Junction area dependence of critical current density in Bi-2212 stacked junction
Kawae, T
Inomata, K
Kim, SJ
Latyshev, YI
Nakajima, K
Yamashita, T
Kishida, S
Hatano, T
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2001, 14 (12): : 1102 - 1105

← 1 2 3 4 5 →