Influence of Ag substrates on grain alignment and critical current density of Bi-2212 tape conductors

被引：0

作者：

Kumakura, H. ^{[1
]}

Kitaguchi, H. ^{[1
]}

Togano, K. ^{[1
]}

Muroga, T. ^{[1
]}

Sato, J. ^{[1
]}

Okada, M. ^{[1
]}

机构：

[1] Natl Research Inst for Metals, Ibaraki, Japan

来源：

IEEE Transactions on Applied Superconductivity | 1999年 / 9卷 / 2 II期

关键词：

Bismuth compounds - Coating techniques - Critical current density (superconductivity) - Crystal impurities - Crystal microstructure - Interfaces (materials) - Silver - Superconducting films - Surface roughness - Tapes - X ray diffraction;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

We investigated the influence of Ag substrate on the microstructure and Jc values of dip-coated Bi-2212/Ag tapes. The grain alignment of Bi-2212 in the oxide/Ag interface was much higher than that in the free surface of oxide. Jc increases with increasing oxide/Ag interface area and with decreasing oxide layer thickness, while Jc was almost independent of the free surface area. The smoothness of the Ag substrate is also an important factor. Micrometer-size roughness of the Ag substrate results in a decrease of Bi-2212 grain alignment and therefore Jc. Addition of alloying elements to the Ag also degrades the grain alignment of Bi-2212 and decreased Jc. Cold rolling before the heat treatment improved the grain alignment and enhanced Jc.

引用

页码：1804 / 1807

共 50 条

[11] Bi-2212/Ag Tape Conductor and Coil Development
Albert, G. W.
Zhou, R.
Leung, E. M.
Salazar, K. V.
Advances in Cryogenic Engineering, (41/A):
[12] Bi-2212/Ag tape conductor and coil development
Albert, GW
Zhou, R
Leung, EM
Salazar, KV
Holesinger, TG
Daugherty, MD
Willis, JO
ADVANCES IN CRYOGENIC ENGINEERING, VOL 41, PTS A AND B, 1996, : 419 - 425
[13] Fabrication of laminated Bi-2212/Ag multifilamentary tape
Yuan, DW
Majer, WJ
Francavilla, TL
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (03): : 287 - 290
[14] The influence of Ag on Bi-2212 and Bi-2223
Majewski, P
Aubele, A
Aldinger, F
PHYSICA C, 2000, 341 : 517 - 518
[15] An anomaly in current-voltage characteristics of Ag-sheathed Bi-2212 tape
Matsumoto, Y.
Nishida, T.
Sakamoto, N.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1994, 235-40 : 3103 - 3104
[16] Understanding and mitigating strain effects in Bi-2212/Ag conductors
Damborsky, Kyle
Parrell, Jeff
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2015, 28 (05):
[17] Spatial distribution of the critical current density in superconducting Bi-2212 strips
Fizika Nizkikh Temperatur (Kiev), 1996, 22 (09):
[18] Spatial distribution of the critical current density in superconducting Bi-2212 strips
Pan, AV
Ionescu, M
Dou, SX
FIZIKA NIZKIKH TEMPERATUR, 1996, 22 (09): : 1022 - 1027
[19] Critical current density and flux pinning in Bi-2212 superconducting thick film grown on oxidized Ni tape
Ni, BR
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 386 : 300 - 303
[20] The effect of oxygen partial pressure and cooling rate during processing on the critical current density and grain coupling of Bi-2212/Ag tapes
Fujii, H
Nakane, T
Kumakura, H
Yamaguchi, H
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (02): : 233 - 236

← 1 2 3 4 5 →