Oxidation and hot corrosion of gradient thermal barrier coatings prepared by EB-PVD

被引：0
|
作者：
Guo, Hongbo [1 ]
Gong, Shengkai [1 ]
Xu, Huibin [1 ]
机构：
[1] Sch. of Mat. Sci. and Eng., Beijing Univ. of Aero. and Astron., Beijing 100083, China
来源：
Journal of Materials Science and Technology | 2002年 / 18卷 / 01期
关键词：
Alumina - Corrosion - Oxidation - Turbomachine blades - Vapor deposition;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The performances of gradient thermal barrier coatings (GTBCs) produced by EB-PVD were evaluated by isothermal oxidation and cyclic hot corrosion (HTHC) tests. Compared with conventional two-layered TBCs, the GTBCs exhibit better resistance to oxidation and hot-corrosion. A dense Al2O3 layer in the GTBCs effectively prohibits the 0 and S inward diffusion and the Al and Cr outward diffusion during the tests. On the other hand, an inlaid interface, resulting from the oxidation of the Al along the columnar grains of the bond coat, enhances the adherence of the Al2O3 layer. The failure of the GTBC can finally occur by cracking at the interface between the bond coat and the Al2O3 layer, due to the combined effect of sulfidation of the bond coat and thermal cycling.
引用
收藏
页码：27 / 30
相关论文
共 50 条
  • [31] Effects of the substrate temperature on microstructure and property of EB-PVD gradient thermal barrier coatings
    Guo, H.
    Xu, H.
    Gong, S.
    Liu, F.
    Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (09): : 997 - 1000
  • [32] Effects of the substrate temperature on microstructure and property of EB-PVD gradient thermal barrier coatings
    Guo, HB
    Xu, HB
    Gong, SK
    Liu, FS
    ACTA METALLURGICA SINICA, 2001, 37 (09) : 997 - 1000
  • [33] Hot Corrosion of an EB-PVD Thermal-Barrier Coating System at 950°C
    C. Leyens
    I. G. Wright
    B. A. Pint
    Oxidation of Metals, 2000, 54 : 401 - 424
  • [34] Experimental and computational study on hot fatigue process of thermal barrier coatings by EB-PVD
    Xu, HB
    Gong, SK
    Zhang, Y
    Zhang, CX
    INTERMETALLICS, 2005, 13 (3-4) : 315 - 322
  • [35] Hot corrosion of an EB-PVD thermal-barrier coating system at 950°C
    Leyens, C
    Wright, IG
    Pint, BA
    OXIDATION OF METALS, 2000, 54 (5-6): : 401 - 424
  • [36] Distribution of residual stresses in EB-PVD thermal barrier coatings
    Suzuki, Kenji
    Shobu, Takahisa
    Tanaka, Keisuke
    STRESS EVALUATION IN MATERIALS USING NEUTRONS AND SYNCHROTRON RADIATION, 2008, 571-572 : 333 - +
  • [37] EB-PVD thermal barrier coatings for aeroengines and gas turbines
    Peters, M
    Leyens, C
    Schulz, U
    Kaysser, WA
    ADVANCED ENGINEERING MATERIALS, 2001, 3 (04) : 193 - 204
  • [38] Nanostructured thermal barrier coatings by APS and EB-PVD and their properties
    Beijing Institute of Aeronautical Materials, Beijing 100095, China
    不详
    不详
    Hangkong Cailiao Xuebao, 2006, 3 (157-162):
  • [39] Infrared radiative properties of EB-PVD thermal barrier coatings
    Yang, G.
    Zhao, C. Y.
    INTERNATIONAL JOURNAL OF HEAT AND MASS TRANSFER, 2016, 94 : 199 - 210
  • [40] EB-PVD zirconia thermal barrier coatings for experiments in space
    Lugscheider, E
    Doepper, G
    Mayer, HG
    Seidel, A
    Dreier, W
    HIGH TEMPERATURE SURFACE ENGINEERING, 2000, : 77 - 84
12345