Oxidation and hot corrosion of gradient thermal barrier coatings prepared by EB-PVD

被引：0

作者：

Guo, Hongbo ^{[1
]}

Gong, Shengkai ^{[1
]}

Xu, Huibin ^{[1
]}

机构：

[1] Sch. of Mat. Sci. and Eng., Beijing Univ. of Aero. and Astron., Beijing 100083, China

来源：

Journal of Materials Science and Technology | 2002年 / 18卷 / 01期

关键词：

Alumina - Corrosion - Oxidation - Turbomachine blades - Vapor deposition;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The performances of gradient thermal barrier coatings (GTBCs) produced by EB-PVD were evaluated by isothermal oxidation and cyclic hot corrosion (HTHC) tests. Compared with conventional two-layered TBCs, the GTBCs exhibit better resistance to oxidation and hot-corrosion. A dense Al2O3 layer in the GTBCs effectively prohibits the 0 and S inward diffusion and the Al and Cr outward diffusion during the tests. On the other hand, an inlaid interface, resulting from the oxidation of the Al along the columnar grains of the bond coat, enhances the adherence of the Al2O3 layer. The failure of the GTBC can finally occur by cracking at the interface between the bond coat and the Al2O3 layer, due to the combined effect of sulfidation of the bond coat and thermal cycling.

引用

页码：27 / 30

共 50 条

[21] INVESTIGATIONS　ON　THE　FORMATION　OF　INITIAL　CRACKS　IN　THERMAL　BARRIER　COATINGS　PREPARED　BY　EB－PVD
S.K.Gong
L. Deng
F.S.Liu and H.B.Xu(Department of Material Science and Engineering
ActaMetallurgicaSinica(EnglishLetters), 1996, (06) : 519 - 522
[22] Residual stress in EB-PVD thermal barrier coatings
Suzuki, Kenji
Tanaka, Keisuke
Shobu, Takahisa
RESIDUAL STRESSES VII, 2006, 524-525 : 879 - 884
[23] Oxidation and thermal fatigue of EB-PVD thermal barrier coatings on tube superalloy substrate
Gao Yu
Zhang Chun-xia
Zhou Chun-gen
Gong Sheng-kai
Xu Hui-bin
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S10 - S13
[24] Graded thermal barrier coatings, deposited by EB-PVD
Movchan, BA
Yakovchuk, KY
SURFACE & COATINGS TECHNOLOGY, 2004, 188 : 85 - 92
[25] Thermal conductivity issues of EB-PVD thermal barrier coatings
Schulz, U.
Raeitzer-Scheibe, H.-J.
Saruhan, B.
Renteria, A. F.
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2007, 38 (09) : 659 - 666
[26] Isothermal oxidation behavior of a thermal barrier coating prepared using EB-PVD
Chen, Zhaoyun
Dong, Zichao
SURFACE AND INTERFACE ANALYSIS, 2015, 47 (03) : 377 - 383
[27] Thermal shock behavior of EB-PVD thermal barrier coatings
Li, Meiheng
Sun, Xiaofeng
Hu, Wangyu
Guan, Hengrong
SURFACE & COATINGS TECHNOLOGY, 2007, 201 (16-17): : 7387 - 7391
[28] Low thermal conductivity EB-PVD thermal barrier coatings
Nicholls, JR
Lawson, KJ
Johnstone, A
Rickerby, DS
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 : 595 - 606
[29] Thermal cycling and isothermal oxidation behavior of quadruple EB-PVD thermal barrier coatings
Bobzin, K.
Broegelmann, T.
Kalscheuer, C.
Yildirim, B.
Welters, M.
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2017, 48 (06) : 502 - 518
[30] Thermal cycling of EB-PVD/NiCoCrAlYHf thermal barrier coatings
Xu, Q. G.
Lu, F.
Wu, X. R.
MATERIALS SCIENCE AND TECHNOLOGY, 2007, 23 (03) : 264 - 269

← 1 2 3 4 5 →