Analysis of the structure of 08Kh18N10T welded joint

被引：0

作者：

Apasov, A.M. ^{[1
]}

Kozlov, E.V. ^{[1
]}

Apasov, A.A. ^{[1
]}

机构：

[1] Filial, Tomskijo Politekhnicheskijo Univ., Yurga, Russia

来源：

Metallovedenie i Termicheskaya Obrabotka Metallov | 2001年 / 12期

关键词：

Phase composition - Stainless steel - Steel metallography - Strength of materials - Welded steel structures - Welds;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

A comparative research of dislocation structure and phase composition of the base metal, near-seam and weld are carried out for specimens of 08Kh18N10T steel. The electron microscopic and x-ray diffraction analyses of welded structure showed that the redistribution of alloying elements in the seam volume and near-seam zone occurs. This induces the qualitative and quantitative changing in phase composition as compared with initial state. An amount of TiC increases and great amount of α-phase, localized at the γ-phase grain boundaries, appears. These factors as well as low residual stresses and grain refinement cause high mechanical properties of weld metal.

引用

页码：19 / 22

共 50 条

[31] Corrosion cracking of welded joints of pipelines from steel 08Kh18N10T in power units with RBMK-type reactors
Zubchenko, A. S.
Kharina, I. L.
Runov, A. E.
Mukhin, A. V.
Korovin, N. Yu.
METAL SCIENCE AND HEAT TREATMENT, 2007, 49 (1-2) : 82 - 88
[32] Corrosion cracking of 08Kh18N10T steel in conditions of steam-generator operation at NPP
Melekhov, R.K.
Smiyan, O.D.
Fiziko-Khimicheskaya Mekhanika Materialov, 1994, 30 (01): : 113 - 122
[33] Viscoplastic Model for the Strain Resistance of 08Kh18N10T Steel at a Hot-Deformation Temperature
Konovalov, A. V.
Smirnov, A. S.
RUSSIAN METALLURGY, 2008, (02): : 138 - 141
[34] EAC of austenitic steel 08Kh18N10T in the steam generator concentrated solutions at 270°C
Brozová, A
Splíchal, K
CORROSION IN REFINERY PETROCHEMICAL AND POWER GENERATION PLANTS, PROCEEDINGS, 2000, : 183 - 188
[35] ON THE STABILITY OF THE STRUCTURE AND PROPERTIES OF BRAZED JOINTS IN 08KH18N10T STEEL DURING LONG-TERM HEATING AND LOADING
ORLOV, AV
PETRUNIN, IE
GURA, PM
MELAMED, MM
KRAVTSOVA, TN
KHARCHEVNIKOV, VA
WELDING PRODUCTION, 1981, 28 (10): : 11 - 13
[36] INFLUENCE OF WELD-INDUCED STRESSES ON INTER-CRYSTALLINE CORROSION OF 08KH18N10T AND 03KH18N11 STEELS
KUZYUKOV, AN
PROTECTION OF METALS, 1978, 14 (04): : 351 - 353
[37] COMPARATIVE INVESTIGATION OF CORROSION OF SHEET AND SECTION ROLLED STEELS 12KH18N10T, 08KH18N10T, AND 03KH23N6 IN BOILING NITRIC-ACID
KONSTANTINOVA, EV
MUKHLYNINA, TA
FELDGANDLER, EG
PROTECTION OF METALS, 1984, 20 (04): : 470 - 472
[38] FORCE PARAMETERS IN THE EXTRUSION OF TUBES FROM A CENTRIFUGALLY CAST SEMIFINISHED PRODUCT OF STEEL 08Kh18N10T
Barichko, B. V.
Vydrin, A. V.
Kosmatskii, Ya. I.
Voskhodov, V. B.
Zubkov, A. M.
METALLURGIST, 2011, 55 (3-4) : 271 - 273
[39] COMPARATIVE-EVALUATION OF THE POSSIBILITY OF USING CERTAIN WELDING MATERIALS FOR WELDING 08KH18N10T STEEL
KNAP, I
AUTOMATIC WELDING USSR, 1986, 39 (05): : 41 - 42
[40] INFLUENCE OF DEGREE OF COLD-ROLLING REDUCTION ON TEXTURE OF THIN STEEL 08KH18N10T SHEET
VOROBEV, GM
BELCHENKO, GI
SHULIKA, NA
KHAVALDZHI, VA
RUSSIAN METALLURGY, 1987, (01): : 58 - 60

← 1 2 3 4 5 →