Effect of the Graphite Compactness on the Mechanical Properties of Vermicular Cast Iron.

被引：0
|
作者：
Dinescu, L.
Craciunescu, C.
Haltrich, K.
Dumitrescu, C.
Bojin, D.
机构：
来源：
Metalurgia Bucuresti | 1982年 / 34卷 / 11期
关键词：
METALLOGRAPHY; -; Microstructures;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The mechanical and technological properties of cast iron largely depend on the shape of the graphite obtained in the solidification process. By controlling the degree of compactness of the graphite precipitations in the structure of vermicular cast iron, it is possible to obtain the desired physicomechanical properties. Studies have shown that, if the nodular graphite rate increases by 2. 54 for a given chemical composition and a given structure, the tensile strength increases from 373 to 590 N/mm**2, while the elongation increases by 5. 8.
引用
收藏
页码：597 / 603
相关论文
共 50 条
  • [11] Vermicular Graphite Cast Iron: Properties, Manufacture, Application.
    Scheinert, Harald
    Liesenberg, Otto
    1978, 24 (04): : 108 - 112
  • [12] EFFECT OF THE SHAPE OF GRAPHITE AND OF THE DISPERSITY OF MARTENSITE ON THE MECHANICAL PROPERTIES OF HIGH-STRENGTH CAST IRON.
    Yakovlev, F.I.
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1986, 28 (5-6): : 378 - 380
  • [13] The effect of vermicularity on the thermal conductivity of vermicular graphite cast iron
    Ma, Z. J.
    Tao, D.
    Yang, Z.
    Guo, Y. C.
    Li, J. P.
    Liang, M. X.
    Yeung, Lugee T. Li
    MATERIALS & DESIGN, 2016, 93 : 418 - 422
  • [14] The Effect of Sulphur Content on the Microstructure of Vermicular Graphite Cast Iron
    Mroz, M.
    Orlowicz, A. W.
    Tupaj, M.
    Lenik, M.
    Kawinski, M.
    ARCHIVES OF FOUNDRY ENGINEERING, 2022, 22 (01) : 18 - 22
  • [15] RESEARCH ON THE COMPACTED/VERMICULAR GRAPHITE CAST IRON MANUFACTURED BY GAS BLOWING INTO MAGNESIUM TREATED MOLTEN IRON.
    Tsutsumi, Nobuhisa
    Chino, Morimasa
    Furuya, Sakae
    Report of the Castings Research Laboratory, Waseda University, 1984, (35): : 33 - 46
  • [16] INFLUENCE OF THE SHAPE OF GRAPHITE INCLUSIONS ON THE STRESS CONCENTRATION AND MECHANICAL PROPERTIES OF CAST IRON.
    Volchok, I.P.
    Stadnik, M.M.
    Silovanyuk, V.P.
    Yuzvak, V.M.
    Kolotilkin, O.B.
    1984, (20):
  • [17] Investigation, by Impact Test, of the Failure of a Vermicular Graphite Iron.
    Konecna, R.
    Habashi, M.
    Skocovsky, P.
    Fonderie-Fondeur d'Aujourd'hui, 1985, (48): : 32 - 37
  • [18] EFFECTS OF ELASTICITY AND COMPACTNESS OF GRAPHITES ON THE FATIGUE STRENGTH OF SPHEROIDAL GRAPHITE CAST IRON.
    Yano, Mitsuru
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (481): : 2150 - 2154
  • [19] GRAPHITE GROWTH IN CAST IRON.
    McSwain, R.H.
    Bates, C.E.
    AFS International Cast Metals Journal, 1976, 1 (01): : 53 - 57
  • [20] Growth mechanisms of vermicular graphite in cast iron
    Lin, Xiaohang
    Hua, Minghao
    Tian, Xuelei
    Jiang, Ailong
    Li, Shuo
    Zhang, Xiaofu
    Song, Lin
    Shao, Anchen
    Wang, Lei
    MATERIALS TODAY COMMUNICATIONS, 2021, 29
12345