High-deposition-rate growth of lead titanate zirconate films by reactive electron beam coevaporation

被引：0
|
作者：
机构：
[1] Mochizuki, Shoichi
[2] Mihara, Toshiyuki
[3] Ishida, Tadashi
来源：
Mochizuki, Shoichi | 1600年 / JJAP, Minato-ku, Japan卷 / 33期
关键词：
Annealing - Electron beams - Evaporation - Ferroelectric materials - Ozone - Perovskite - Phase transitions - Semiconducting lead compounds - Semiconductor growth - Titanate minerals - Vapor deposition - Zirconium compounds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Lead titanate zirconate (PZT) thin films were prepared by reactive coevaporation of lead, zirconium and titanium with an electron beam gun. To promote oxygenation of deposited films, mixed gas of oxygen and ozone was used. A PZT film with a single perovskite phase was obtained at a substrate temperature of 550 °C without post-thermal annealing on a lead titanate film. The deposition rate was 50 nm/min, which was much higher than that in the case of the sputtering method. The axial ratio (c/a) of the tetragonal perovskite phase decreased with the increase of zirconium content.
引用
收藏
相关论文
共 50 条
  • [31] Electron beam deposited lead-lanthanum-zirconate-titanate thin films for silicon based device applications
    J Appl Phys, 2 (1008):
  • [32] Electron beam deposited lead-lanthanum-zirconate-titanate thin films for silicon based device applications
    Panda, B
    Ray, SK
    Dhar, A
    Sarkar, A
    Bhattacharya, D
    Chopra, KL
    JOURNAL OF APPLIED PHYSICS, 1996, 79 (02) : 1008 - 1012
  • [33] High reliable lead-zirconate-titanate growth using reactive sputtering and rapid thermal annealing
    Yamauchi, S
    Yoshimaru, M
    INTEGRATED FERROELECTRICS, 1997, 14 (1-4) : 159 - 166
  • [34] Growth and measurements of ferroelectric lead zirconate titanate on diamond by pulsed laser deposition
    Du, H
    Johnson, DW
    Zhu, W
    Graebner, JE
    Kammlott, GW
    Jin, S
    Rogers, J
    Willett, R
    Fleming, RM
    JOURNAL OF APPLIED PHYSICS, 1999, 86 (04) : 2220 - 2225
  • [35] Polarization reorientation in ferroelectric lead zirconate titanate thin films with electron beams
    Li, DB
    Strachan, DR
    Ferris, JH
    Bonnell, DA
    JOURNAL OF MATERIALS RESEARCH, 2006, 21 (04) : 935 - 940
  • [36] Polarization reorientation in ferroelectric lead zirconate titanate thin films with electron beams
    Li D.B.
    Strachan D.R.
    Ferris J.H.
    Bonnell D.A.
    Journal of Materials Research, 2006, 21 (4) : 935 - 940
  • [37] Processing of high performance lead lanthanum zirconate titanate thick films
    Kosec, M
    Holc, J
    Malic, B
    Bobnar, V
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (6-7) : 949 - 954
  • [38] INSITU GROWTH OF SUPERCONDUCTING YBACUO USING REACTIVE ELECTRON-BEAM COEVAPORATION
    MISSERT, N
    HAMMOND, R
    MOOIJ, JE
    MATIJASEVIC, V
    ROSENTHAL, P
    GEBALLE, TH
    KAPITULNIK, A
    BEASLEY, MR
    LADERMAN, SS
    LU, C
    GARWIN, E
    BARTON, R
    IEEE TRANSACTIONS ON MAGNETICS, 1989, 25 (02) : 2418 - 2421
  • [39] Preparation of lead zirconate titanate thin films by reactive magnetron co-sputtering
    Yamakawa, K
    TrolierMcKinstry, S
    Dougherty, JP
    MATERIALS LETTERS, 1996, 28 (4-6) : 317 - 322
  • [40] Effects of deposition temperature and seed layer on the optical properties of lead zirconate titanate films
    Kang, HS
    Lee, WJ
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2002, 20 (04): : 1498 - 1504
12345